Tytuł:: Zmodyfikowana technologia wytwarzania korpusów marszowych silników rakietowych
Modified Technology for Production of Rocket Engines Bodies
Autorzy:: Burdek, M.
Stępień, J.
Wójtowicz, W.
Powiązania:: https://bibliotekanauki.pl/articles/403382.pdf
Data publikacji:: 2010
Wydawca:: Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego
Tematy:: technologia
korpus silnika rakietowego
stal maraging
product engineering
body of rocket engine
maraging steel
Opis:: Artykuł zawiera wyniki prac zrealizowanych we współpracy Instytutu Metalurgii Żelaza i Zakładów Metalowych "Mesko" S.A., dotyczących opracowania i zastosowania nowoczesnych wyrobów stalowych ze stali typu maraging do wytwarzania korpusów rakiet o podwyższonych właściwościach mechanicznych.
Results of investigation concerning development and application of modern steel products made of maraging grade of higher mechanical properties for production of rocket engines bodies, carried out together by Institute for Ferrous Metallurgy in Gliwice, Poland and Metal Works "MESKO" S.A. in Skarżysko-Kamienna, Poland, are presented in this paper.
Źródło:: Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa; 2010, 1, 1 (1); 79-84
2081-5891
Pojawia się w:: Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Korpusy startowych silników rakietowych ze stali "maraging"
Bodies of Rato Booster Rockets Made of Maraging Steel
Autorzy:: Stępień, J.
Marcisz, J.
Garbarz, B.
Burdek, M.
Moskalewicz, M.
Wójtowicz, W.
Patek, A.
Materniak, J.
Powiązania:: https://bibliotekanauki.pl/articles/403851.pdf
Data publikacji:: 2012
Wydawca:: Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego
Tematy:: inżynieria materiałowa
stal maraging
silnik rakietowy
korpus silnika startowego
materials engineering
maraging steel
RATO booster rockets
Opis:: Artykuł zawiera wyniki prac zrealizowanych we współpracy Zakładów Metalowych MESKO, Instytutu Metalurgii Żelaza i Politechniki Poznańskiej, dotyczących opracowania i zastosowania nowoczesnych wyrobów stalowych do wytwarzania korpusów rakiet. Badania przeprowadzono w celu opracowania i wdrożenia technologii wytwarzania korpusów rakietowych silników startowych z krążków wyciętych z blachy walcowanej na zimno ze stali "maraging" zamiast ze stali 28H3SNMWFAŻ (SP28Ż). Opracowano skład chemiczny stali "maraging" o symbolu N18K9M5Ts oraz wymagania w zakresie właściwości mechanicznych przed poszczególnymi operacjami technologii wytwarzania korpusów rakietowych silników startowych. Wykonano badania podstawowych właściwości fizycznych stali "maraging" N18K9M5Ts wytworzonej w IMŻ w piecu próżniowym VSG 100S, w celu przygotowania bazy danych do projektowania technologii przeróbki plastycznej i obróbki cieplnej. Wyznaczono temperatury przemian fazowych, opracowano charakterystyki odkształcalności na zimno oraz ustalono parametry przesycania i utwardzania wydzieleniowego.
The paper presents the results of examinations carried out to determine thepossibilities of application of super-clean 300 ksi maraging steel instead of 28H3SNMWFAŻ steel to produce the bodies of RATO booster rockets. The studies of basic physical properties, cold formability, temperatures of phase transformations, and parameters of precipitation hardening of 300 ksi maraging steel were carried out.
Źródło:: Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa; 2012, 3, 2 (8); 99-108
2081-5891
Pojawia się w:: Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 3.

Tytuł:: Short-Time Ageing of MS350 Maraging Steel with and Without Plastic Deformation
Krótkotrwałe starzenie stali maraging MS350 w warunkach odkształcenia plastycznego
Autorzy:: Marcisz, J.
Stępień, J.
Powiązania:: https://bibliotekanauki.pl/articles/354104.pdf
Data publikacji:: 2014
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: maraging steel
short-time ageing
flow forming
precipitation kinetics
HRTEM
stal maraging
krótkotrwałe starzenie
odkształcenie plastyczne
Opis:: The age hardening behaviour of MS350 maraging steel both in undeformed specimens and in specimens deformed immediately after ageing was studied. Experiments of short-time (15, 30 and 60 s) ageing at temperature up to 600°C were performed. It was found that after ageing at 480-500°C for 15-60 s without deformation the hardness reached the 450-525 HV. The time of ageing at 600°C to reach hardness 600 HV was 15 seconds. No precipitation in specimen aged at 500°C for 60 s was found in TEM and HRTEM investigations. Deformation immediately after ageing intensifies the process of hardening caused by temporary increase of temperature and increase of dislocation density. The hardness of specimens aged for 30 s and then deformed at 480-550°C was similar to the hardness at peak aged conditions (480°C/4h) and reached 600-630 HV. Material produced in industrial trials of cold forward flow forming and following laboratory ageing was analyzed. Increase of hardness from 370 HV to 590-630 HV for specimens taken from thin walled flow formed tube as a result of ageing at 460-490°C for 30 minutes occurred.
Przedstawiono wyniki badań procesu starzenia stali maraging w gatunku MS350 dla próbek nieodkształconych i odkształconych bezpośrednio po starzeniu. Przeprowadzono eksperymenty starzenia krótkotrwałego (15. 30 i 60 s) w temperaturze do 600°C. Stwierdzono, że po starzeniu w zakresie temperatury 480-500<,C w czasie 15-60 s bez odkształcenia, twardość osiągnęła 450-525 HV. Czas starzenia w temperaturze 600°C do osiągnięcia twardości 600 HV wynosił 15 s. Nie stwierdzono wydzieleń w próbkach starzonych w temperaturze 500°C przez 60 s w badaniach z zastosowaniem wysokorozdzielczego transmisyjnego mikroskopu elektronowego. Odkształcenie bezpośrednio po starzeniu intensyfikuje proces umacniania wydzieleniowego w skutek chwilowego wzrostu temperatury oraz wyrost u gęstości dyslokacji. Twardość próbek starzonych przez 30 s i odkształcanych w zakresie temperatury 480- 500“^ była zbliżona do twardości uzyskiwanej dla warunków starzenia w celu uzyskania twardości maksymalnej (480°C/4godz.) i wynosiła 600-630 HV. Przeprowadzono badania materiału wytwarzanego w próbach przemysłowych zgniatania obrotowego i starzonego w warunkach laboratoryjnych. Dla próbek pobranych z rury cienkościennej uzyskano wzrost twardości z 370 HV do 590-630 HV w wyniku starzenia w zakresie temperatury 460-490°C przez 30 minut.
Źródło:: Archives of Metallurgy and Materials; 2014, 59, 2; 513-520
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 4.

Tytuł:: Kinetyka wydzielania oraz właściwości stali maraging po krótkotrwałym starzeniu
Precipitation kinetics and properties of maraging steel after short-time ageing
Autorzy:: Marcisz, J.
Garbarz, B.
Adamczyk, M.
Stępień, J.
Powiązania:: https://bibliotekanauki.pl/articles/181786.pdf
Data publikacji:: 2012
Wydawca:: Sieć Badawcza Łukasiewicz - Instytut Metalurgii Żelaza im. Stanisława Staszica
Tematy:: stal maraging
starzenie krótkotrwałe
nagrzewanie indukcyjne
mikrostruktura
transmisyjny mikroskop elektronowy
maraging steel
short-time ageing
induction heating
microstructure
transmission electron microscope
Opis:: W pracy podjęto badania skutków wczesnych etapów umacniania wydzieleniowego ultrawysokowytrzymałych stali maraging MS350 i MS550. Badano zmiany struktury i właściwości w początkowych stadiach starzenia. Wyniki badań będą wykorzystane do modyfikacji technologii wytwarzania wyrobów ze stali maraging.
In this paper, testing of the effects of early stages of precipitate strengthening of ultra-highstrength maraging steels MS350 and MS550 was presented. The changes in structure and properties in the initial stages of ageing were tested. Test results will be used for modification of the technology for manufacturing of maraging steel products.
Źródło:: Prace Instytutu Metalurgii Żelaza; 2012, T. 64, nr 4, 4; 18-22
0137-9941
Pojawia się w:: Prace Instytutu Metalurgii Żelaza
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "maraging steel" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język