Wyszukujesz frazę "carbide-free bainite" wg kryterium: Temat


Wyświetlanie 1-2 z 2
Tytuł:
Nanocrystalline Steels’ Resistance to Hydrogen Embrittlement
Odporność na kruchość wodorową stali nanokrystalicznych
Autorzy:
Skołek, E.
Marciniak, S.
Skoczylas, P.
Kamiński, J.
Świątnicki, W. A.
Powiązania:
https://bibliotekanauki.pl/articles/351874.pdf
Data publikacji:
2015
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
carbide-free bainite
tool steel
austempering
hydrogen embrittlement
bainit bezwęglikowy
stal narzędziowa
hartowanie
kruchość wodorowa
Opis:
The aim of this study is to determine the susceptibility to hydrogen embrittlement in X37CrMoV5-1 steel with two different microstructures: a nanocrystalline carbide-free bainite and tempered martensite. The nanobainitic structure was obtained by austempering at the bainitic transformation zone. It was found, that after hydrogen charging, both kinds of microstructure exhibit increased yield strength and strong decrease in ductility. It has been however shown that the resistance to hydrogen embrittlement of X37CrMoV5-1 steel with nanobainitic structure is higher as compared to the tempered martensite. After hydrogen charging the ductility of austempered steel is slightly higher than in case of quenched and tempered (Q&T) steel. This effect was interpreted as a result of phase composition formed after different heat treatments.
Celem pracy było określenie wrażliwości na kruchość wodorową stali X37CrMoV5-1 o dwóch różnych mikrostrukturach: nanokrystalicznego bainitu bezwęglikowego i odpuszczonego martenzytu. Struktura nanobainityczna została otrzymana w wyniku procesu hartowania izotermicznego w zakresie przemiany bainitycznej. Zaobserwowano, że po procesie katodowego nasycania wodorem oba typy mikrostruktury wykazują zwiększenie granicy plastyczności i znaczący spadek plastyczności. Wykazano jednak, że odporność na kruchość wodorową stali X37CrMoV5- 1o strukturze nanobainitycznej jest lepsza w porównaniu do stali o strukturze martenzytu odpuszczonego. Po katodowym nasycaniu wodorem plastyczność stali hartowanej izotermicznie jest nieznacznie wyższa niż w przypadku stali hartowanej i odpuszczanej (Q&T). Zjawisko to zostało zinterpretowane jako wynik składu fazowego wytworzonego podczas różnych obróbek cieplnych.
Źródło:
Archives of Metallurgy and Materials; 2015, 60, 1; 491-496
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Thermal Stability of Nanocrystalline Structure In X37CrMoV5-1 Steel
Stabilność cieplna struktury nanokrystalicznej w stali X37CrMoV5-1
Autorzy:
Skołek, E.
Marciniak, S.
Świątnicki, W. A.
Powiązania:
https://bibliotekanauki.pl/articles/354372.pdf
Data publikacji:
2015
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
nanocrystalline structure
carbide-free bainite
tool steel
thermal stability
TEM
struktura nanokrystaliczna
bainit bezwęglikowy
stal narzędziowa
stabilność cieplna
Opis:
The aim of the study was to investigate the thermal stability of the nanostructure produced in X37CrMoV5-1 tool steel by austempering heat treatment consisted of austenitization and isothermal quenching at the range of the bainitic transformation. The nanostructure was composed of bainitic ferrite plates of nanometric thickness separated by thin layers of retained austenite. It was revealed, that the annealing at the temperature higher than temperature of austempering led to formation of cementite precipitations. At the initial stage of annealing cementite precipitations occurred in the interfaces between ferritic bainite and austenite. With increasing temperature of annealing, the volume fraction and size of cementite precipitations also increased. Simultaneously fine spherical Fe7C3 carbides appeared. At the highest annealing temperature the large, spherical Fe7C3 carbides as well as cementite precipitates inside the ferrite grains were observed. Moreover the volume fraction of bainitic ferrite and of freshly formed martensite increased in steel as a result of retained austenite transformation during cooling down to room temperature.
Celem pracy było zbadanie stabilności cieplnej nanostruktury wytworzonej w stali narzędziowej X37CrMoV5-1 za pomocą obróbki cieplnej polegającej na austenityzacji i hartowaniu z przystankiem izotermicznym w zakresie przemiany bainitycznej. Utworzona nanostruktura składała się z płytek ferrytu bainitycznego nanometrycznej grubości rozdzielonych cienkimi warstwami austenitu szczątkowego. Ujawniono, że wyżarzanie stali w temperaturze wyższej niż temperatura przystanku izotermicznego prowadzi do wytworzenia w nanostrukturze wydzielenia cementytu. W początkowym etapie wyżarzania wydzielenia cementytu utworzyły się na granicach ferrytu bainitycznego i austenitu. Ze wzrostem temperatury wyżarzania następował wzrost udziału objętościowego i wielkości wydzieleń cementytu. Jednocześnie pojawiły się drobne wydzielenia węglika Fe7C3. Po wyżarzaniu w jeszcze wyższych temperaturach zaobserwowano duże, kuliste wydzielenia węglika Fe7C3 oraz wydzielenia cementytu w obrębie ziaren ferrytu. udział objętościowy tej fazy w stali. Nastąpił również wzrost udziału objętościowego ferrytu bainitycznego oraz świeżo utworzonego martenzytu w blokach w wyniku przemiany austenitu szczątkowego podczas chłodzenia stali do temperatury pokojowej.
Źródło:
Archives of Metallurgy and Materials; 2015, 60, 1; 511-516
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-2 z 2

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies