Tytuł:
Meta-stable solidification created by the detonation method of coating formation
Autorzy:
Wołczyński, W.
Garzeł, G.
Morgiel, J.
Senderowski, C.
Pawłowski, A.
Powiązania:
https://bibliotekanauki.pl/articles/382812.pdf
Data publikacji:
2012
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
krystalizacja
krzepnięcie szybkie
powłoka Fe-Al
faza amorficzna
theory of crystallization
rapid solidification process
Fe-Al coating
meta-stable phase diagram
amorphous phase
Opis:
Particles of the Fe-Al type (less than 50 m in diameter) were sprayed onto the 045 steel substrate by means of the detonation method. The TEM, SAED and EDX analyses revealed that the Fe-Al particles have been partially melted in the experiment of coating formation. Particle undergone melting even within about 80% of its volume. Therefore, solidification of the melted part of particles was expected. Solidification differed significantly due to a large range of chemical composition of applied particles (from 15 at.% Al up to 63 at.% Al). A single particle containing 63 at.% Al was subjected to the detailed analysis, only. The TEM / SAED techniques revealed in the solidified part of particle three sub-layers: an amorphous phase, [...] , periodically situated FeAl + Fe2Al5 phases, and a non-equilibrium phase, [...]. A hypothesis dealing with the inter-metallic phases formation in such a single particle of the nominal composition No = 0.63 is presented. At first, the solid / liquid system is treated as an interconnection: substrate / liquid / nonmelted particle part . Therefore, it is suggested that the solidification occurs simultaneously in two directions: towards a substrate and towards a non-melted part of particle. The solidification mechanism is referred to the Fe-Al meta-stable phase diagram. It is shown that the melted part of particle solidifies rapidly according to the phase diagram of meta-stable equilibrium and at a significant deviation from the thermodynamic equilibrium.
Źródło:
Archives of Foundry Engineering; 2012, 12, 2; 93-96
1897-3310
2299-2944
Pojawia się w:
Archives of Foundry Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
D-gun Sprayed Fe-Al Single Particle Solidification
Krystalizacja pojedynczej cząstki Fe-Al naniesionej metodą detonacyjną
Autorzy:
Wołczyński, W.
Senderowski, C.
Morgiel, J.
Garzeł, G.
Powiązania:
https://bibliotekanauki.pl/articles/352240.pdf
Data publikacji:
2014
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
Fe-Al coating
Ni-20Cr interlayer
rapid solidification
D-gun spraying
boron localization
competitive growth of phases
powłoki FeAl
międzywarstwy Ni-20Cr
szybkie krzepnięcie
metoda detonacyjna
lokalizacja boru
proces wzrostu faz
Opis:
Some Fe-Al particles less than 50 μm in diameter were deposited onto the steel substrate by means of the D-gun spraying. A solidification mechanism of an individual particle is described. The particle subjected to the description contained nominally 63 at.% Al. The description was preceded by the TEM / SAED analysis of both the Fe-Al coating and Ni-20Cr interlayer. The whole number of the analyzed particles was partially melted during the deposition. The solidification products like: amorphous phase sub-layer, oscillatory sub-layer which contains two types lamellae distributed alternately and typically non-equilibrium phase sub-layer were revealed. In the micro scale, solidification was considered as a process which occurred in two directions: towards the substrate and towards the non-melted particle part. Both solidification processes underwent the positive thermal gradients. The boron addition was localized within the eutectic precipitates pushed and then rejected by the solid/liquid interface of the solidifying non-equilibrium phase. The proposed model is a general one and therefore can be applied to other systems ;description.
Cząstki proszku Fe-Al niniejsze niż 50 μm w średnicy zostały osadzone detonacyjnie na podłożu stalowym. Opisuje się mechanizm krystalizacji pojedynczej cząstki. Cząstki poddane opisowi zawierały nominalnie 63 aL% Al. Opis poprzedzono badaniami struktury metodą TEM / SAED dotyczącymi zarówno powłoki Fe-Al jak i między warstwy Ni-20Cr. Wszystkie analizowane cząstki były częściowo nadtopione podczas osadzania. Zidentyfikowano produkty krystalizacji takie jak: podwarstwę amorficzną, podwarstwę oscylacyjną zawierającą periodycznie ułożone pły tki dwu faz oraz podwarstwę zawierającą fazę typowo nierównowagową. W mikroskali proces wzrostu faz jest analizowany jako zachodzący w dwu kierunkach: w stronę podłoża i w stronę niestopionej części cząstki. Obydwa procesy wzrostu zachodziły w obecności dodatniego gradientu temperatury. Bor dodany do powłoki został zlokalizowany w eutektyce odepchniętej przez front krystalizacji fazy typowo nierównowagowej. Proponowany model ma charakter ogólny i może być zastosowany do opisu innych systemów.
Źródło:
Archives of Metallurgy and Materials; 2014, 59, 1; 211-220
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-2 z 2

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies