Tytuł:: D-gun Sprayed Fe-Al Single Particle Solidification
Krystalizacja pojedynczej cząstki Fe-Al naniesionej metodą detonacyjną
Autorzy:: Wołczyński, W.
Senderowski, C.
Morgiel, J.
Garzeł, G.
Powiązania:: https://bibliotekanauki.pl/articles/352240.pdf
Data publikacji:: 2014
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: Fe-Al coating
Ni-20Cr interlayer
rapid solidification
D-gun spraying
boron localization
competitive growth of phases
powłoki FeAl
międzywarstwy Ni-20Cr
szybkie krzepnięcie
metoda detonacyjna
lokalizacja boru
proces wzrostu faz
Opis:: Some Fe-Al particles less than 50 μm in diameter were deposited onto the steel substrate by means of the D-gun spraying. A solidification mechanism of an individual particle is described. The particle subjected to the description contained nominally 63 at.% Al. The description was preceded by the TEM / SAED analysis of both the Fe-Al coating and Ni-20Cr interlayer. The whole number of the analyzed particles was partially melted during the deposition. The solidification products like: amorphous phase sub-layer, oscillatory sub-layer which contains two types lamellae distributed alternately and typically non-equilibrium phase sub-layer were revealed. In the micro scale, solidification was considered as a process which occurred in two directions: towards the substrate and towards the non-melted particle part. Both solidification processes underwent the positive thermal gradients. The boron addition was localized within the eutectic precipitates pushed and then rejected by the solid/liquid interface of the solidifying non-equilibrium phase. The proposed model is a general one and therefore can be applied to other systems ;description.
Cząstki proszku Fe-Al niniejsze niż 50 μm w średnicy zostały osadzone detonacyjnie na podłożu stalowym. Opisuje się mechanizm krystalizacji pojedynczej cząstki. Cząstki poddane opisowi zawierały nominalnie 63 aL% Al. Opis poprzedzono badaniami struktury metodą TEM / SAED dotyczącymi zarówno powłoki Fe-Al jak i między warstwy Ni-20Cr. Wszystkie analizowane cząstki były częściowo nadtopione podczas osadzania. Zidentyfikowano produkty krystalizacji takie jak: podwarstwę amorficzną, podwarstwę oscylacyjną zawierającą periodycznie ułożone pły tki dwu faz oraz podwarstwę zawierającą fazę typowo nierównowagową. W mikroskali proces wzrostu faz jest analizowany jako zachodzący w dwu kierunkach: w stronę podłoża i w stronę niestopionej części cząstki. Obydwa procesy wzrostu zachodziły w obecności dodatniego gradientu temperatury. Bor dodany do powłoki został zlokalizowany w eutektyce odepchniętej przez front krystalizacji fazy typowo nierównowagowej. Proponowany model ma charakter ogólny i może być zastosowany do opisu innych systemów.
Źródło:: Archives of Metallurgy and Materials; 2014, 59, 1; 211-220
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Meta-stable solidification created by the detonation method of coating formation
Autorzy:: Wołczyński, W.
Garzeł, G.
Morgiel, J.
Senderowski, C.
Pawłowski, A.
Powiązania:: https://bibliotekanauki.pl/articles/382812.pdf
Data publikacji:: 2012
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: krystalizacja
krzepnięcie szybkie
powłoka Fe-Al
faza amorficzna
theory of crystallization
rapid solidification process
Fe-Al coating
meta-stable phase diagram
amorphous phase
Opis:: Particles of the Fe-Al type (less than 50 m in diameter) were sprayed onto the 045 steel substrate by means of the detonation method. The TEM, SAED and EDX analyses revealed that the Fe-Al particles have been partially melted in the experiment of coating formation. Particle undergone melting even within about 80% of its volume. Therefore, solidification of the melted part of particles was expected. Solidification differed significantly due to a large range of chemical composition of applied particles (from 15 at.% Al up to 63 at.% Al). A single particle containing 63 at.% Al was subjected to the detailed analysis, only. The TEM / SAED techniques revealed in the solidified part of particle three sub-layers: an amorphous phase, [...] , periodically situated FeAl + Fe2Al5 phases, and a non-equilibrium phase, [...]. A hypothesis dealing with the inter-metallic phases formation in such a single particle of the nominal composition No = 0.63 is presented. At first, the solid / liquid system is treated as an interconnection: substrate / liquid / nonmelted particle part . Therefore, it is suggested that the solidification occurs simultaneously in two directions: towards a substrate and towards a non-melted part of particle. The solidification mechanism is referred to the Fe-Al meta-stable phase diagram. It is shown that the melted part of particle solidifies rapidly according to the phase diagram of meta-stable equilibrium and at a significant deviation from the thermodynamic equilibrium.
Źródło:: Archives of Foundry Engineering; 2012, 12, 2; 93-96
1897-3310
2299-2944
Pojawia się w:: Archives of Foundry Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 3.

Tytuł:: Detonation deposited Fe-Al coatings. Part II: Transmission electron microscopy of interlayers and Fe-Al intermetallic coating detonation sprayed onto the 045 steel substrate
Detonacyjne osadzanie warstw Fe-Al. Część II: Transmisyjna mikroskopia elektronowa warstw pośrednich oraz powłoki faz typu Fe-Al natryskiwanych detonacyjnie na podłoże stali 045
Autorzy:: Pawłowski, A.
Senderowski, C.
Wołczyński, W.
Morgiel, J.
Major, Ł.
Powiązania:: https://bibliotekanauki.pl/articles/354124.pdf
Data publikacji:: 2011
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: natryskiwanie detonacyjne
powłoki międzymetaliczne
D-gun spraying
Fe-Al intermetallic coatings
Ni(Al) and Cr(Al) interlayers
Opis:: The microstructure of detonation gaseous sprayed (DGS) transition layers of Ni(Al), Ni(Cr) and subsequent coating of Fe-Al intermetallic phases deposited on the 045 steel were studied in the paper using transmission electron microscopy. In order to identify phases in the particular interlayers the selected area electron diffraction (SAED) and an energy dispersive X-ray microanalysis (EDX) were applied. It was found that the Ni(Al) interlayer contained basically pure nickel with a small fraction of NiAl phase. The Al based amorphous phase was also observed its area in the form of bands. The Ni(Cr) interlayer basically contained Ni-rich small grains. Pure chromium in the Ni matrix appeared in the vicinity of Fe-Al coating in the shape of bow-like bands, parallel to the coating. The boundary between the Ni(Cr) layer and the Fe-Al coating revealed abrupt decrease of the Ni content in the coating at simultaneous rapid increase of the Fe amount. Improper Al/Cr ratio within the Ni matrix seems to be responsible for the formation of Al-oxides and the bands of almost pure Cr and Ni(Cr) layers and resulting decrease of interlayer adherence.
W pracy analizowano mikrostrukturę złożonej budowy wielowarstwy składającej się z podłoża ze stali węglowej 045 oraz osadzonych detonacyjnie (DGS) na niej warstw pośrednich Ni(Al) i Ni(Cr) oraz powłoki faz międzymetalicznych typu Fe-Al. W celu identyfikacji faz powłoki i warstw pośrednich zastosowano techniki badawcze: dyfrakcji elektronowej (SAED) oraz analizy składu chemicznego faz (EDX) w transmisyjnym mikroskopie elektronowym. Stwierdzono, że warstwa Ni(Al) zawiera przede wszystkim prawie czysty nikiel z małym udziałem fazy NiAl. Oprócz tego w obszarze ziaren Ni występowała faza amorficzna w postaci pasm oparta na Al i O. Obecność niewielkich rozmiarów ziaren bogatych w nikiel stwierdzono również w warstwie Ni(Cr), wewnątrz których znajdowały się pasma czystego chromu. Granica pomiędzy Ni(Cr) oraz powłoką Fe-Al wykazywała gwałtowny spadek zawartości niklu przy jednoczesnym silnym wzroście żelaza. Obecność tlenków aluminium oraz pasm bogatych w chrom wynikała z niewłaściwych proporcji Al/Cr podczas przygotowania wielowarstw i wpływała negatywnie na ilość mikropęknięć i porów oraz wynikającą z tego adhezję pomiędzy poszczególnymi warstwami.
Źródło:: Archives of Metallurgy and Materials; 2011, 56, 1; 71-79
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Morgiel, J" wg kryterium: Autor

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język