Autor: Szala, Mirosław - Katalog OPAC zbiorów

Skocz do pozycji: 1.

Tytuł:: Innovative device for tensile strength testing of welded joints: 3d modelling, FEM simulation and experimental validation of test rig – a case study
Autorzy:: Sawa, Mateusz
Szala, Mirosław
Henzler, Weronika
Powiązania:: https://bibliotekanauki.pl/articles/1956076.pdf
Data publikacji:: 2021
Wydawca:: Polskie Towarzystwo Promocji Wiedzy
Tematy:: tensile strength
FEM
CAD modelling
stainless steel
mechanical engineering
wytrzymałość na rozciąganie
MES
modelowanie CAD
stal nierdzewna
inżynieria mechaniczna
Opis:: This work shows a case study into 3D modelling, numerical simulations, and preliminary research of self-designed test rig dedicated for uniaxial tensile testing using pillar press. Innovative device was CAD modelled, FEM optimized, build-up according to the technological documentations. Then, the device utilization for tensile testing was validated via preliminary research. 3D model of the device was designed and FEM-analyzed using Solid Edge 2020 software. The set of FEM simulations for device components made ofstructuralsteel and stainless steel and at a workload equal 20 kN were conducted. This made it possible to optimize dimensions and selection of material used for individual parts of the device structure. Elaborated technical documentation allows for a buildup of a device prototype which was fixed into the pillar press. After that, the comparative preliminary experiments regarding tensile strength tests of X5CrNi18-10 (AISI 304) specimens were carried out. Tests were done using the commercial tensile strength machine and obtained results were compared with those received from an invented device. The ultimate tensile strength of X5CrNi18-10 steel, estimated using the commercial device (634 MPa) and results obtained from the patented device (620 MPa), were in the range of the standardized values. Findings confirm the utilization of the invented device for tensile strength testing.
Źródło:: Applied Computer Science; 2021, 17, 3; 92-105
1895-3735
Pojawia się w:: Applied Computer Science
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Influence of austenitic interlayer on the properties of stellite padding welds after impact-hardening
Ocena wpływu międzywarstwy austenitycznej na właściwości napoin stellitowych utwardzonych udarowo
Autorzy:: Henzler, Weronika
Sawa, Mateusz
Trębicki, Przemysław
Szala, Mirosław
Winiarski, Grzegorz
Powiązania:: https://bibliotekanauki.pl/articles/1819232.pdf
Data publikacji:: 2021
Wydawca:: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
Tematy:: stellit
napawanie TIG
warstwa buforowa
twardość
umocnienie udarowe
młot resorowy
stellite
TIG cladding
interlayer
hardness
impact hardening
spring hammer
Opis:: Stellites (Co-Cr-W-C) are the specific group of coating materials used for surface modification of the engineering materials and for remanufacturing. The aim of the paper was to research the influence of austenitic (308LSi) interlayer on hardening rate of stellite 1 and stellite 6 after impact hardening. The samples have been cladded by TIG welding method with interlayer and without. Before impact hardening the samples have been visually and penetrant non-destructive tested. The samples after impact hardening have been tested by metallographic and Vickers hardness methods. The highest impact hardening effect have been revealed for coatings deposited with interlayer. The highest impact hardening effect was achieved for the padding welds produced with the interlayer, i.e. for stellite 1 (increased by 29.8%) and stellite 6 (increased by 42.7%). The hardening of the coating samples deposited without interlayer was lower and amounted to stellite 1 (increased by 13.7%) and stellite 6 (increased by 29.8%) respectively. The highest hardness values were obtained for impact-hardened cladded welds without the use of an interlayer (stellite 1; 790 HV0.1 and stellite 6; 732 HV0.1). The use of an interlayer reduces the hardness of the stellite coating while increasing the susceptibility to hardening and plastic deformation of the produced coating.
Stellity (Co-Cr-W-C) stanowią grupę materiałów stosowanych do napawania produkcyjnego i regeneracyjnego. Celem pracy było zbadanie wpływu międzywarstwy austenitycznej (308LSi) na stopień umocnienia się napoin stellitowych (stellit 1 i stellit 6), poddanych działaniu obciążeń udarowych. Próbki napawano metodą TIG z zastosowaniem międzywarstwy oraz bez udziału międzywarstwy. Po przeprowadzeniu badań wizualnych i penetracyjnych próbki zostały poddane utwardzeniu udarowemu. Wykonano badania metalograficzne oraz badania mikrotwardości sposobem Vickersa. Największe utwardzenie udarowe uzyskano dla napoin wytworzonych z międzywarstwą, tj. dla stellitu 1: 29.8% i stellitu 6: 42.7%. Utwardzenie próbek napawanych bez międzywarstwy było niższe i wynosiło kolejno dla stellitu 1: 13.7% i stellitu 6: 29.8%. Najwyższe wartości twardości uzyskano dla napoin utwardzanych udarowo bez zastosowania międzywarstwy (stellit 1; 790 HV0,1 i stellit 6; 732 HV0,1). Zastosowanie międzywarstwy obniża mikrotwardość powłoki stellitowej jednocześnie zwiększając podatność do umocnienia i odkształcenia plastycznego wytworzonej powłoki.
Źródło:: Welding Technology Review; 2021, 93, 2; 13--20
0033-2364
2449-7959
Pojawia się w:: Welding Technology Review
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Szala, Mirosław" wg kryterium: Autor

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język