Autor: Moraczewski, R. - Katalog OPAC zbiorów

Skocz do pozycji: 1.

Tytuł:: Autocatalytic metallization of polylactide
Autokatalityczne metalizowanie polilaktydu
Autorzy:: Moraczewski, K.
Malinowski, R.
Rytlewski, P.
Żenkiewicz, M.
Powiązania:: https://bibliotekanauki.pl/articles/947500.pdf
Data publikacji:: 2015
Wydawca:: Sieć Badawcza Łukasiewicz - Instytut Chemii Przemysłowej
Tematy:: polylactide
chemical modification
autocatalytic metallization
polilaktyd
modyfikacja chemiczna
metalizowanie autokatalityczne
Opis:: In this work experimental results of a research aimed to provide the assessment of the ability of chemical modification to prepare polylactide (PLA) surface for autocatalytic metallization are presented. Chemical modification of PLA was performed using two solutions (1 and 2). Analysis of PLA samples was performed by means of goniometry, atomic force microscopy (AFM), scanning electron microscopy (SEM) and photoelectron spectroscopy (XPS). Results of contact angle measurements and surface energy calculations were presented. Qualitative and quantitative analysis of elemental composition of PLA surface layer was performed. Based on the experimental results, it was found that the proposed method can be successfully applied to prepare PLA surface for metallization. Autocatalytically deposited copper layer exhibited good adhesion to PLA and electrical conductivity.
Zbadano możliwość wykorzystania modyfikacji chemicznej w procesie przygotowania powierzchni polilaktydu (PLA) do procesu autokatalitycznego metalizowania. Modyfikację chemiczną PLA przeprowadzono za pomocą dwóch roztworów (1 i 2). Próbki PLA zbadano metodami: goniometrii, mikroskopii sił atomowych (AFM), elektronowej mikroskopii skaningowej (SEM) i spektroskopii fotoelektronowej (XPS). Wykonano też pomiary kątów zwilżania oraz obliczenia swobodnej energii powierzchniowej, a także przeprowadzono jakościową i ilościową analizę składu chemicznego warstwy wierzchniej PLA. Wyniki badań wskazują, że zaproponowana metoda może być wykorzystana w procesie przygotowania powierzchni polilaktydu PLA do metalizowania. Uzyskana warstwa metaliczna charakteryzuje się dobrą wytrzymałością adhezyjną i dobrymi właściwościami elektrycznymi.
Źródło:: Polimery; 2015, 60, 7-8; 492-500
0032-2725
Pojawia się w:: Polimery
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Mechanical properties and biodegradability of flax fiber-reinforced composite of polylactide and polycaprolactone
Właściwości mechaniczne i biodegradowalność wzmocnionego włóknami lnianymi kompozytu polilaktydu z polikaprolaktonem
Autorzy:: Rytlewski, P.
Stepczyńska, M.
Moraczewski, K.
Malinowski, R.
Jagodziński, B.
Żenkiewicz, M.
Powiązania:: https://bibliotekanauki.pl/articles/947048.pdf
Data publikacji:: 2018
Wydawca:: Sieć Badawcza Łukasiewicz - Instytut Chemii Przemysłowej
Tematy:: polylactide
polycaprolactone
flax fibers
mechanical properties
biodegradation
polilaktyd
polikaprolakton
włókna lniane
właściwości mechaniczne
biodegradacja
Opis:: The aim of this work was to produce a composite based on the blend of polylactide and polycaprolactone and reinforced with flax fiber, intended for processing by injection molding, with improved mechanical and biodegradation properties as compared to neat polylactide (PLA) and polycaprolactone (PCL). The material was prepared by mixing PLA, PCL and flax fibers (about 5 mm long), extrusion and granulation with subsequent injection molding to obtain test samples. The composites differed in the content of PCL (0, 5, 10, 15 and 30 wt %) whereas the content of flax fibers was kept constant (20 wt %). The samples were characterized by means of scanning electron microscopy (SEM), tensile and impact strength measurements, differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). Biodegradation studies were carried out using proteinase K at laboratory conditions. It was found that a reduction of fiber lengths took place during the extrusion process and that addition of flax fibers to PLA/PCL blend resulted in an increase in elastic modulus and biodegradation rate. The composite impact strength was significantly improved at 30 wt % PCL fraction.
Celem badań było opracowanie kompozytu wzmocnionego włóknem lnianym na osnowie z mieszaniny polilaktyd/polikaprolakton, przeznaczonego do przetwórstwa metodą wtryskiwania, wykazującego lepsze właściwości mechaniczne oraz lepszą biodegradowalność niż niemodyfikowane polilaktyd (PLA) i polikaprolakton (PCL). Materiał przygotowano metodą wytłaczania. PLA, PCL oraz włókna lniane (o długości około 5 mm) mieszano, wytłaczano, granulowano, a następnie wtryskiwano w celu uzyskania próbek do badań. Kompozyty różniły się zawartością PCL (0, 5, 10, 15 lub 30% mas.), natomiast udział procentowy włókien lnianych był stały (20% mas.). Próbki badano metodami: skaningowej mikroskopii elektronowej (SEM), różnicowej kalorymetrii skaningowej (DSC) oraz dynamicznej analizy mechanicznej (DMA). Oceniano też ich wytrzymałość na jednoosiowe rozciąganie i udarność. Podatność na biodegradację badano w warunkach laboratoryjnych z zastosowaniem enzymu proteinazy K. Stwierdzono, że w procesie wytłaczania nastąpiła znaczna redukcja długości włókien lnianych, ich dodatek do mieszaniny PLA/PCL wpłynął na zwiększenie modułu sprężystości i szybkości biodegradacji, a udział 30% mas. PCL wyraźnie poprawił udarność kompozytu.
Źródło:: Polimery; 2018, 63, 9; 603-610
0032-2725
Pojawia się w:: Polimery
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Moraczewski, R." wg kryterium: Autor

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język