Tytuł:
The effect of Sm addition on the microstructure and superconducting properties of YBCO bulk superconductors
Autorzy:
Volochová, D.
Diko, P.
Piovarči, S.
Antal, V.
Kováč, J.
Jirsa, M.
Powiązania:
https://bibliotekanauki.pl/articles/1054772.pdf
Data publikacji:
2017-04
Wydawca:
Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:
74.72.-h
74.62.Dh
81.10.Fq
61.72.-y
74.25.Ha
74.25.Sv
Opis:
The effect of Sm addition on the microstructure and superconducting properties of Y-Ba-Cu-O (YBCO) bulk superconductors has been studied. Nominal composition: 1 mol YBa₂Cu₃O_{7-δ} + 0.25 mol Y₂O₃ + 1 wt% CeO₂ was enriched with different amounts of SmBa₂Cu₃O_y powder with the aim to increase critical current density, J_c, especially in higher magnetic fields by introducing additional pinning centers. Single grain YBCO bulk superconductors with SmBa₂Cu₃O_y (Y123-Sm) addition were prepared by the optimized top seeded melt growth process. Microstructure analysis, performed by polarized light microscope, revealed that SmBa₂Cu₃O_y addition leads to a higher amount of slightly coarser Y₂BaCuO₅ particles, which is related to lower critical current densities (J_c ≈ 6×10⁴ A/cm²) of the YBCO samples with SmBa₂Cu₃O_y addition in low magnetic fields. On the other hand, an enhancement of critical current density, J_c, in higher magnetic fields was observed for Y123-Sm samples. Moreover, a maximum trapped magnetic field, B_{tmax}, of 564 mT at 77 K in Y123-Sm, x=0.0025 sample (Ø 17.2 mm) was 43% higher than that for YBCO sample without any addition.
Źródło:
Acta Physica Polonica A; 2017, 131, 4; 1009-1011
0587-4246
1898-794X
Pojawia się w:
Acta Physica Polonica A
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Trapped field of YBCO bulk superconductors prepared by infiltration growth process
Autorzy:
Vojtkova, L.
Diko, P.
Piovarči, S.
Powiązania:
https://bibliotekanauki.pl/articles/1054776.pdf
Data publikacji:
2017-04
Wydawca:
Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:
74.72.-h
74.81.Bd
61.50.-f
74.25.Ha
81.10.Fq
Opis:
Single grain Y₁Ba₂Cu₃O_{7-x} (YBCO) bulk superconductors were prepared from different starting precursors. In the first case, Y₂Ba₁Cu₁O₅ (Y211) powder as the solid phase and the liquid phase of mixture of YBa₂Cu₃O_{7-x}+BaCuO₂+CuO powders were used. In the second case, the solid phase was prepared from the mixture of Y₂O₃+BaCuO₂ instead of the conventionally used Y211, and as the liquid phase a mixture of Y₂O₃+BaCuO₂+CuO powders was used. The trapped field measurements at 77 K were performed and microstructure of samples was studied by polarized light microscopy. The positive influence of Y₂O₃+BaCuO₂ starting precursor on the oxygenation, Y211 particle refinement and measured trapped field is shown.
Źródło:
Acta Physica Polonica A; 2017, 131, 4; 1048-1050
0587-4246
1898-794X
Pojawia się w:
Acta Physica Polonica A
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-2 z 2

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies