    Tytuł:
    Influence of Processing Parameters and Different Content of TiB2 Ceramics on the Properties of Composites Sintered by High Pressure -High Temperature (HP-HT) Method
    Wpływ parametów procesu oraz ceramiki TiB2 na właściwości kompozytów spiekanych metodą wysokociśnieniową (HP-HT)
    Autorzy:
    Sulima, I.
    Jaworska, L.
    Figiel, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/351634.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    titanium diboride (TiB2)
    high pressure-high temperature sintering
    austenitic stainless steel
    properties
    spiekanie metodą wysokociśnieniową
    ceramika TiB2
    stal austenityczna
    właściwości
    Opis:
    In this paper the properties of the austenitic stainless steel reinforced with various volume fractions of TiB2 ceramics have been studied. The high pressure- high temperature (HP-HT) method of sintering was applied to the formation of composites. Samples were sintered at pressure of 5 and 7 ±0.2 GPa and temperatures of 1273 K and 1573 K. For the tested materials, the relative density, Young’s modulus and hardness were measured. In order to investigate the structure changes, the scanning electron microscope was used. The obtained results show that the temperature and pressure influence on the mechanical and physical properties of the investigated composites.
    W prezentowanej pracy zbadano właściwości stali austenitycznej z różnym udziałem objętościowym ceramiki TiB2. Do wytworzenia spieków kompozytowych proszków zastosowano spiekanie wysokociśnieniowe HP-HT. Próbki były spiekane przy ciśnieniu 5 oraz 7±0.2 GPa i temperatururze 1273 K oraz 1573 K. Kompozyty poddano badaniom gęstości, modułu Younga oraz twardości. Badania mikrostruktury przeprowadzono za pomocą skaningowej mikroskopii elektronowej. Uzyskane wyniki badań wykazały, że temperatura oraz ciśnienie wpływają na mechaniczne oraz fizyczne wł aściwości materiałów kompozytowych.
    Źródło:
    Archives of Metallurgy and Materials; 2014, 59, 1; 205-209
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Characteristics of the NiAl/Ni3Al Matrix Composite with TiB2 Particles Fabricated by High Pressure - High Temperature Sintering
    Autorzy:
    Hyjek, P.
    Sulima, I.
    Jaworska, L.
    Powiązania:
    https://bibliotekanauki.pl/articles/352345.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    sintering
    High Pressure High Temperature process
    metal matrix composites
    tribological properties
    Opis:
    The article presents the results of tests carried out on the manufactured composite materials based on a two-phase NiAl/Ni3Al matrix, which was enriched with the addition of TiB2 ceramic particles added in an amount of 4 and 7 vol%. The resulting mixtures were sintered by the High Pressure High Temperature (HP-HT) process. The results were compared to the results obtained for the sole matrix material produced under the same conditions. It has been shown that, at a lower density, the addition of reinforcing particles increases the composite hardness, Young’s modulus and resistance to frictional wear. However, higher addition of TiB2 (7 vol%) was observed to yield less satisfactory results, and despite higher hardness and lower density caused a decrease in other properties tested. The produced materials were characterized by a compact and highly differentiated microstructure free from any noticeable cracks and pores.
    Źródło:
    Archives of Metallurgy and Materials; 2017, 62, 3; 1511-1520
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Influence of High Pressure-High Temperature Method on the Selected Mechanical Properties of Steel AISI 316L with 2% TiB2
    Autorzy:
    Kurtyka, P.
    Sulima, I.
    Hyjek, P.
    Jaworska, L.
    Powiązania:
    https://bibliotekanauki.pl/articles/356857.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    high pressure-high temperature
    physical properties
    mechanical properties
    steel matrix composites
    titanium diboride
    Opis:
    AISI 316L/TiB2/2p composites were manufactured by HP-HT using different pressures (5 and 7 GPa) and temperatures (900-1300°C), with constant reinforcing particle content 2 vol%. The mechanical properties of the composites were evaluated on the basis of hardness (HV0.3) and compression tests (20°C, 10-5 s-1). The results showed that the role of sintering pressure increased with increasing process temperature. At temperatures of 900°C and pressures of 5 and 7 GPa the difference in measured values of compressive strength was 1-2%, while at 1300°C they reached 20%. At constant pressure of 5 GPa, a change in hardness and compressive strength of 40% were obtained with a temperature change of 900 to 1300°C. Changes in mechanical properties in the composite occurred without substantial changes in density, microstructure, reinforcement phase distribution, and phase composition in the matrix.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 4; 1585-1592
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies