Evaluation of selected properties and surface quality of cured pre-impregnated carbon-fiber fabrics after exposure to sulphuric acid
Autorzy:
Kojnoková, Tatiana
Nový, František
Markovičová, Lenka
Harea, Evgheni
Harea, Evghenii
Powiązania:
https://bibliotekanauki.pl/articles/26081735.pdf
Data publikacji:
2023
Wydawca:
Stowarzyszenie Menedżerów Jakości i Produkcji
Tematy:
tkaniny węglowe
żywica epoksydowa
zmiana wagi
jakość powierzchni
carbon fabrics
epoxy resin
micro-hardness
weight change
surface quality
Opis:
This paper deals with changes in selected properties of composite material and surface degradation after exposure to an acidic environment. A carbon fiber-reinforced composite (CFRP) produced from prepregs was tested. The weight change, micro-hardness, and surface degradation of the CFRP composite made of cured pre-impregnated laminates were evaluated in this study. Material consisting of a DT121R epoxy resin matrix with high reactivity and high viscosity, with two reinforcing carbon fabrics layers, is characterized by a low value of tensile strength. Evaluation of changes in the material properties was performed before and after exposure to specific environmental conditions, which are achieved by using a chemical solution of 15% H2SO4 at various temperatures. Subsequently, the effect of 15% H2SO4 at various temperatures on the material properties was monitored. The specimens were immersed in the solution for up to 3 and 6 weeks at the temperatures of 23°C, 40°C, and 60°C. It was found out, that the degradation of the composite material is conditioned by the aging of the epoxy resin (matrix). Carbon fibers (reinforcement) are relatively stable. The weight change, micro-hardness, and surface quality depend on the time of exposure to acidic solution and temperature. The micro-hardness tests show a significant influence on exposure time. The biggest changes in weight change and surface quality of the CFRP composite were observed after exposure at the temperature of 60°C.
Źródło:
Production Engineering Archives; 2023, 29, 1; 1--6
2353-5156
2353-7779
Pojawia się w:
Production Engineering Archives
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies