- Tytuł:
- Stress corrosion cracking of welded joints of Al-Mg alloys
- Autorzy:
- Czechowski, M.
- Powiązania:
- https://bibliotekanauki.pl/articles/241941.pdf
- Data publikacji:
- 2014
- Wydawca:
- Instytut Techniczny Wojsk Lotniczych
- Tematy:
-
stress corrosion cracking
welding
aluminium alloy
friction stir welding (FSW) - Opis:
- Slow strain rate testing (SSRT) was used to test the stress corrosion cracking (SCC) of aluminium alloys AW 5083 and AW 5059 (Alustar) jointed by friction stir welding (FSW). The test was carried out in the air and 3.5% water solution NaCl. Cylindrical notch-free specimens and cylindrical notched specimens (R = 5 mm) were used. The following parameters were measured: time-to-failure – T [h], obtained max. load – F [N]; strain energy (the diagram surface under the stress-elongation curve) – E [MAJ/m3]; relative elongation of the specimen – A11.3 [%]; max. tensile stress – R [MPa] and narrowing – Z [%]. On the basis of obtained results, it was noted that FSW-welded joints show superior strength and resistance to stress corrosion, compared to MIG-welded joints. The fractions after SSRT testing were cleaved with some ductile areas. This article also gives the mechanical features of friction stir welded Al-Mg alloys. Tests have shown that the 5059 alloy, welded by FSW, has superior strength properties compared to the FSW 5083 alloy, along with comparable, good resistance to stress corrosion. FSW 5083 alloy joints have very good resistance to stress corrosion - better than those made using traditional welding methods (MUG). Original value are received results of the stress corrosion resistance of new method friction stir welded Al-Mg alloy compared with traditional MIG method.
- Źródło:
-
Journal of KONES; 2014, 21, 3; 41-45
1231-4005
2354-0133 - Pojawia się w:
- Journal of KONES
- Dostawca treści:
- Biblioteka Nauki
Artykuł