Tytuł:
A study on damage to PLA knitted fabrics during scouring and bleaching
Autorzy:
Baig, G. A.
Carr, C. M.
Powiązania:
https://bibliotekanauki.pl/articles/778625.pdf
Data publikacji:
2014
Wydawca:
Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie
Tematy:
PLA
Scouring
Bleaching
Weight loss
mechanical properties
SEM
Opis:
Ingeo® PLA (polylactic acid) knitted fabric was scoured through an exhaust technique. The scouring was carried out with sodium carbonate in the presence of a detergent at various concentrations and temperatures. The scoured fabric was bleached with various oxidative bleaching agents. Bleaching was carried out with hydrogen peroxide, sodium chlorite and sodium hypochlorite. Hydrogen peroxide was applied by exhaust and cold pad batch (CPB) techniques. It was observed that during scouring PLA fabric was degraded at high alkali concentrations and processing temperatures. The scouring temperature above 60oC proved to be deleterious due to the scouring solution penetrating into the polymer structure and damaged the fiber. Sodium chlorite and sodium hypochlorite caused little damage to the mechanical properties of PLA. Hydrogen peroxide when applied by the CPB technique did not reduce strength appreciably but when applied by the exhaust technique decreased the strength significantly. SEM analysis revealed that hydrogen peroxide caused holes and slit formation in the fiber structure.
Źródło:
Polish Journal of Chemical Technology; 2014, 16, 3; 45-50
1509-8117
1899-4741
Pojawia się w:
Polish Journal of Chemical Technology
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Surface and Structural Damage to PLA Fibres during Textile Pretreatments
Uszkodzenia powierzchni i struktury włókien PLA podczas wstępnej obróbki
Autorzy:
Baig, G. A.
Carr, C. M.
Powiązania:
https://bibliotekanauki.pl/articles/234194.pdf
Data publikacji:
2016
Wydawca:
Sieć Badawcza Łukasiewicz - Instytut Biopolimerów i Włókien Chemicznych
Tematy:
PLA
renewable polymer
scouring
bleaching
tensile properties
SEM
IR
XPS
polimery odnawialne
czyszczenie
bielenie
właściwości mechaniczne przy rozciąganiu
Opis:
PLA knitted fabric was treated with sodium carbonate in the presence of non-ionic detergent at various concentrations and temperatures in a short liquor bath. The scoured fabric was subsequently treated with industrially important bleaching agents such as hydrogen peroxide, sodium chlorite and sodium hypochlorite at various levels of concentration and pH. The bleached PLA fabric was then evaluated in terms of surface and bulk properties. The structural damage was assessed in terms of tensile strength, while the surface morphology was investigated using scanning electron microscopy (SEM). The surface chemistry of PLA was studied using infra-red (IR) and x-ray photoelectron spectroscopies (XPS). The alkaline-oxidative conditions were deleterious to the integrity of PLA polymer at high temperature, while at low temperature there was a little damage. The acidic-oxidative conditions did not appreciably affect bulk or surface properties even at high temperature.
Dzianiny wykonane z PLA poddano obróbce węglanem sodu w obecności niejonowych detergentów przy rożnych stężeniach i temperaturach. Dzianiny były równocześnie poddane działaniu przemysłowo ważnych środków bielących, takich jak: nadtlenek wodoru, chloryn sodu i podchloryn sodu przy rożnych poziomach stężenia i pH. Bielone dzianiny PLA były następnie oceniane biorąc pod uwagę właściwości powierzchni i wnętrza. Strukturalne uszkodzenia wewnętrzne były oceniane poprzez wytrzymałość na rozciąganie, podczas gdy morfologię powierzchni badano za pomocą SEM. Powierzchnie dzianin PLA badano również stosując spektrofotometrie IR i XPS. Działanie środków alkalicznych i utleniających miało wpływ uszkadzający na integralność polimeru PLA przy wyższych temperaturach, podczas gdy przy niskich temperaturach uszkodzenia były niewielkie.
Źródło:
Fibres & Textiles in Eastern Europe; 2016, 2 (116); 52-58
1230-3666
2300-7354
Pojawia się w:
Fibres & Textiles in Eastern Europe
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-2 z 2

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies