- Microstructure of the Bonding Zone Between AZ91 and AlSi17 Formed by Compound Casting
- Autorzy:
-
Mola, R.
Bucki, T.
Dziadoń, A. - Powiązania:
- https://bibliotekanauki.pl/articles/379744.pdf
- Data publikacji:
- 2017
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
casting process
joining
magnesium alloys
aluminum alloys
intermetallic phases
microstructure
proces odlewania
łączenie
stop magnezu
stop aluminium
faza intermetaliczna
mikrostruktura - Opis:
- This paper discusses the joining of AZ91 magnesium alloy with AlSi17 aluminium alloy by compound casting. Molten AZ91 was cast at 650oC onto a solid AlSi17 insert placed in a steel mould under normal atmospheric conditions. Before casting, the mould with the insert inside was heated up to about 370oC. The bonding zone forming between the two alloys as a result of diffusion had a multiphase structure and a thickness of about 200 μm. The microstructure and composition of the bonding zone were analysed using optical microscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The results indicate that the bonding zone adjacent to the AlSi17 alloy was composed of an Al3Mg2 intermetallic phase with not fully consumed primary Si particles, surrounded by a rim of an Mg2Si intermetallic phase and fine Mg2Si particles. The bonding zone near the AZ91 alloy was composed of a eutectic (an Mg17Al12 intermetallic phase and a solid solution of Al and Si in Mg). It was also found that the compound casting process slightly affected the AZ91alloy microstructure; a thin layer adjacent to the bonding zone of the alloy was enriched with aluminium.