- Tytuł:
- Magnetic Properties and Structure of Amorphous $Fe_{74}Hf_{4}Ta_{1}Cu_{1}Gd_{1}La_{x}Si_{15-x}B_{4}$ (x = 0, 7) Ribbons
- Autorzy:
-
Bardziński, P.
Kopcewicz, M.
Rybaczuk, M.
Hasiak, M.
Musiał, A.
Kinzhybalo, V.
Idzikowski, B. - Powiązania:
- https://bibliotekanauki.pl/articles/1399300.pdf
- Data publikacji:
- 2015-03
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
75.50.-y
75.50.Bb
75.50.Kj
75.60.Ej
81.05.Kf
82.80.Ej
61.05.Qr - Opis:
- The multi component $Fe_{74}Hf_{4}Ta_{1}Cu_{1}Gd_{1}La_{x}Si_{15-x}B_{4}$ (x = 0, 7) alloys are promising candidates in the search for materials with unusual mechanical and magnetic properties. Amorphous nature of melt-spun samples was confirmed by X-ray diffractometry and Mössbauer spectroscopy. The X-ray diffraction patterns revealed a distinct amorphous halo. The low-field components of magnetic hyperfine field distributions on iron nuclei are observed in the Mössbauer spectra, with average hyperfine field values of 19.9 and 15.7 T for x = 0 and x = 7, respectively. Coercivity studied by vibrating sample magnetometer was about 12 A/m for x = 0 and 82 A/m for x = 7 at 300 K and about 600 A/m for x = 0 and 1200 A/m for x = 7 at 400 K. Remanence also changed with temperature, amounting to 0.64 T for x = 0 and 0.36 T for x = 7 at 300 K, while at 400 K it was 0.43 and 0.11 T for x = 0 and x = 7, respectively. It is shown that La addition has beneficial effect of shifting the Curie point towards lower temperatures together with the increase of magnitude of magnetization.