Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "Bala, A." wg kryterium: Autor

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-6 z 6
    Tytuł:
    The Mössbauer Spectroscopy Studies οf Cementite Precipitations during Continuous Heating from As-Quenched State of High Carbon Cr-Mn-Mo Steel
    Autorzy:
    Krawczyk, J.
    Bała, P.
    Hanc, A.
    Powiązania:
    https://bibliotekanauki.pl/articles/1811613.pdf
    Data publikacji:
    2008-12
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    76.80.+y
    31.30.Gs
    75.50.Bb
    Opis:
    This work complements the knowledge concerning the kinetics of cementite precipitation during tempering. Investigations were performed on 120MnCrMoV8-6-4-2 steel. The samples of investigated steel were austenitized at the temperature of 900°C and quenched in oil. Then four of five samples were tempered. Tempering consisted of heating the samples up to chosen temperatures at the heating rate of 0.05°C/s and fast cooling after reaching desired temperature. This work presents the results of investigations performed carried out using the Mössbauer spectroscopy technique and their interpretation concerning cementite nucleation and growth during tempering. The values of hyperfine magnetic field on $\text{}^{57}Fe$ atomic nuclei, determined for the third component of the Mössbauer spectrum as regards to its intensity, indicate that these are the components coming from ferromagnetic carbides. Big differences in hyperfine magnetic fields coming from Fe atoms existing in the structure of carbides, measured on samples heated up to the temperatures of 80°C and 210°C, in comparison with values for $\text{}^{57}Fe$ atoms precipitated from carbides during heating up to the temperature of 350°C and 470°C, allow to state that these are the carbides of different crystal structure. The influence of hardened steel heating temperature on cementite precipitation was determined. The Mössbauer spectroscopy was applied not only for magnetic hyperfine fileld studies, but also to analyze the values of quadrupole splitting and isomeric shift, which resulted in significant conclusions concerning the changes in cementite precipitations morphology, chemical composition and the level of stresses being present in this research.
    Źródło:
    Acta Physica Polonica A; 2008, 114, 6; 1651-1657
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Mössbauer Spectroscopy Studies of ϵ to Cementite Carbides Transformation during Isothermal Heating from As-Quenched State οf High Carbon Tool Steel
    Autorzy:
    Bała, P.
    Krawczyk, J.
    Hanc, A.
    Powiązania:
    https://bibliotekanauki.pl/articles/1811611.pdf
    Data publikacji:
    2008-12
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    76.80.+y
    31.30.Gs
    75.50.Bb
    Opis:
    This work presents results of investigations using the Mössbauer spectroscopy technique and their interpretation concerning transformation of ϵ to cementite carbides during tempering in relation to the previously conducted dilatometric, microscopic and mechanical investigations. Investigations were performed on 120MnCrMoV8-6-4-2 steel. The influence of the tempering time on nucleation and solubility of ϵ carbides, and on cementite nucleation and growth, was determined. The analysis of phase transformations during various periods of tempering using the Mössbauer spectroscopy technique made possible to reveal fine details connected with the processes.
    Źródło:
    Acta Physica Polonica A; 2008, 114, 6; 1641-1650
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Charakterystyka zużycia stempla podczas wyciskania stalowych elementów
    The characteristics of the wear of the stamp used in backward extrusion of steel elements
    Autorzy:
    Łukaszek-Sołek, A.
    Krawczyk, J.
    Bednarek, S.
    Sińczak, J.
    Śleboda, T.
    Bała, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/189072.pdf
    Data publikacji:
    2011
    Wydawca:
    Stowarzyszenie Inżynierów i Techników Mechaników Polskich
    Tematy:
    zużycie
    tribologia
    modelowanie numeryczne
    wyciskanie przeciwbieżne
    stal narzędziowa
    wear
    tribology
    numerical modeling
    backward extrusion
    tool steel
    Opis:
    W pracy opisano mechanizm zużycia stempla wykonanego ze stali 32CrMoV12-28 używanego do wyciskania bufora zderzaka kolejowego. Stempel ten uległ pęknięciu, które wyeliminowało go z dalszej eksploatacji. Wykonano charakterystykę materiałową stempla i określono jej wpływ na mechanizm zużycia w odniesieniu do jego warunków pracy. Do powyższej analizy wykorzystano obliczenia numeryczne współczynnika zużycia. Wyniki badań wskazują na istotną rolę tworzenia się tzw. białej warstwy w mechanizmie zużycia tribologicznego oraz inicjacji pęknięcia. Określono rolę mikrostruktury w rozwoju pęknięcia. Wyniki badań pozwolą na dobór lub zaprojektowanie nowych materiałów narzędziowych na tego typu elementy pracujące w szczególnie trudnych tribologicznie warunkach.
    This research is aimed at the analysis of wear mechanisms of 32CrMoV12-28 steel stamp used in extrusion of railway bumpers. The stamp cracked, which excluded it from further use. The analysis of the stamp material was performed and its influence on the wear mechanisms operating under working conditions of the stamp was analyzed. The calculations of the wear factor were also used in this research. The results of this research show that the white layer formation is a very important phenomenon, strongly influencing crack formation in the investigated stamp. The role of the microstructure of the analyzed stamp in the crack development was also investigated. The presented results will allow one to properly select or design new tool steels for the structural parts working under tribologically difficult conditions.
    Źródło:
    Tribologia; 2011, 4; 153-161
    0208-7774
    Pojawia się w:
    Tribologia
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Strain induced recrystallization in hot forged inconel 718 alloy
    Rekrystalizacja stopu inconel 718 indukowana odkształceniem podczas kucia matrycowego
    Autorzy:
    Krawczyk, J.
    Łukaszek-Sołek, A.
    Śleboda, T.
    Bała, P.
    Bednarek, S.
    Wojtaszek, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/355033.pdf
    Data publikacji:
    2012
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Inconel 718
    kucie matrycowe
    mikrostruktury
    hot forging
    recrystallization
    microstructure
    simulations
    Opis:
    Changes in the microstructure of Inconel 718 resulting from hot forging were investigated in this work. Axisymmetrical forging characterized by the areas of different forging reduction ratios was subjected to the analysis. The investigated alloy was forged under various thermomechanical conditions. Two forging modes, differing by the geometry and the temperature of the billet were performed in industrial conditions. It was revealed, that the microstructure of the alloy after forging was in the solutionized condition with different levels of recrystallization determining the differences in the grain size. Moreover, numerous simulations of the analyzed forging process taking into account variable thermomechanical conditions were performed using QForm 3D v. 5.1 software. The results of the simulations were compared with the results of forging the investigated alloy in industrial conditions. These results showed to be in very good agreement with the experimental observations. The changes in the microstructure of the investigated alloy forging were also compared with the results of the performed simulations. This study allowed determining both the influence of chosen thermomechanical parameters on recrystallization process in hot forged Inconel 718 alloy as well as the possibility of obtaining good quality forgings with uniform microstructure out of this alloy.
    W pracy przedstawiono wyniki badań zmian w mikrostrukturze stopu Inconel 718 powstałych w wyniku kucia. Kształtowano odkuwkę o kształcie zbliżonym do osiowosymetrycznego będącej jednocześnie przykładem odkuwki posiadającej obszary charakteryzujące sie różnym stopniem przerobu materiału. Pozwoliło to uzyskać złożone warunki termomechaniczne podczas kucia i po jego zakończeniu. Zastosowano dwa różne wymiary wsadu oraz dwie różne temperatury nagrzania do kucia. Stwierdzono, ze po kuciu mikrostruktura stopu jest w stanie przesyconym z różnym stopniem zaawansowania procesu rekrystalizacji oraz wielkości ziarna po rekrystalizacji. Przeprowadzono również szereg symulacji procesu kucia omawianego materiału w zmiennych warunkach cieplno mechanicznych z zastosowaniem programu QForm 3D v. 5.1. Odniesienie wyników modelowania numerycznego analizowanego procesu przeróbki plastycznej do uzyskanej mikrostruktury odkuwki pozwoliło na przedstawienie koncepcji roli warunków termomechanicznych na proces rekrystalizacji w stopie Inconel 718 oraz określenie możliwości kształtowania odkuwki z tego stopu w celu uzyskania jednorodnej mikrostruktury.
    Źródło:
    Archives of Metallurgy and Materials; 2012, 57, 2; 593-603
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Analiza oddziaływania materiału wsadowego na mechanizm zużycia wkładek matrycowych formujących w procesie kształtowania elementów zderzaka kolejowego
    The analysis of the effect of billet material on the mechanism of wear in forming die inserts in the process of railway bumper formation
    Autorzy:
    Bednarek, S.
    Krawczyk, J.
    Bała, P.
    Łukaszek-Sołek, A.
    Śleboda, T.
    Wojtaszek, M.
    Chyła, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/189096.pdf
    Data publikacji:
    2011
    Wydawca:
    Stowarzyszenie Inżynierów i Techników Mechaników Polskich
    Tematy:
    zużycie
    tribologia
    modelowanie numeryczne
    wyciskanie przeciwbieżne
    stal narzędziowa
    wear
    tribology
    numerical modeling
    backward extrusion
    tool steel
    Opis:
    W pracy omówiono mechanizm zużycia wkładki matrycowej formującej używanej do wyciskania bazy zderzaka kolejowego. Wkładka ta została wykonana ze stali X40CrMoV5-1. Sporządzono charakterystykę materiału, z którego została wykonana badana wkładka matrycowa formująca. Określono rolę mikrostruktury oraz rozszerzalności cieplnej na mechanizm zużycia badanej wkładki. Wyniki badań metaloznawczych mechanizmów zużycia oraz zmian w mikrostrukturze warstwy wierzchniej odniesiono do symulacji opartych na obliczeniach numerycznych współczynnika zużycia. Wyniki badań wskazują na istotną rolę w zużyciu wkładki matrycowej formującej mechanizmów takich jak: tworzenie się białej warstwy, zmęczenie cieplne, utlenianie.
    The mechanism of wear in the forming die insert used for the extrusion of a railway bumper was investigated in this work. The insert was made of X40CrMoV5-1 steel. The analysis of the die insert material was performed. The role of the microstructure and thermal expansion in the mechanisms of wear of the investigated die insert was also studied. The results of metallographical investigations of the mechanisms of wear and changes in the microstructure of the top surface of the die insert were linked to the results of the numerical simulations of the die wear factor. The obtained results indicate that such mechanisms as white layer formation, thermal fatigue, and oxidation, play an important role in the wear of the die insert.
    Źródło:
    Tribologia; 2011, 4; 33-41
    0208-7774
    Pojawia się w:
    Tribologia
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Structures of Cu-based glass forming system doped with iron
    Autorzy:
    Kozieł, T.
    Latuch, J.
    Czeppe, T.
    Ratuszek, W.
    Cios, G.
    Zielińska-Lipiec, A.
    Bała, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/1153737.pdf
    Data publikacji:
    2016-10
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    81.05.Kf
    81.05.Bx
    61.05.cp
    68.37.Hk
    Opis:
    The effects of iron additions on the structure of (Cu_{0.47}Ti_{0.34}Zr_{0.11}Ni_{0.08})_{100-x}Fe_{x} (x=0, 1.5, 3, 6) glass forming system are presented. The alloys were synthesized by arc melting of high purity elements and melt spun to form: rapidly quenched ribbons. X-ray diffraction studies showed the amorphous structure of the base and Fe-containing alloys, confirmed by the presence of exothermic peaks on differential scanning calorimetry curves. Bulk samples in the form of rods (Φ3×55 mm) were cast using a suction casting unit attached to the arc melter. Structural investigations revealed partial crystallization of the base Cu₄₇Ti₃₄Zr₁₁Ni₈ alloy. Iron additions significantly decreased the glass forming ability of the alloy, leading to primary crystallization of dendrites.
    Źródło:
    Acta Physica Polonica A; 2016, 130, 4; 913-915
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-6 z 6

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies