- Tytuł:
- Evaluation the Solidification/Stabilization of Heavy Metals by Portland Cement
- Autorzy:
- Al-Kindi, Ghayda Yaseen
- Powiązania:
- https://bibliotekanauki.pl/articles/124334.pdf
- Data publikacji:
- 2019
- Wydawca:
- Polskie Towarzystwo Inżynierii Ekologicznej
- Tematy:
-
solidification/stabilization
binder
cement
leaching
hazards waste - Opis:
- Numerous solutions are used in the site to treat pollution, including remediation of heavy metals and hazardous wastes by solidification/stabilization (S/S) with cement as a binder. S/S is one of the most commonly methods used for treating inorganic wastes. The objective of this research was using unconfined compressive strength test, and EPA Toxicity Leaching Procedure TCLP method 1313, to test the effectiveness performance, and efficiency of the solidification/stabilization method for treatment of some heavy metals (Fe, Zn, Mn, Cr) contaminated sands using ordinary locally produced Portland Cement type A. In this study, three loads of pollution in three mix designs by contaminated sands were used. As a result of the unconfined compression test, it was observed that the value 1–15 MPa with OPC cement content 25% in the solidification/stabilization process was good enough to comply with the limited value set by the (US EPA). In addition, the concentration of zinc ions was 500 kg/mg, 1500 kg/mg, and 3000 kg/mg, which caused an increase in compressive strength in the early period of age, and a decrease at a later age. An increase in the iron ion concentration caused an increase in the compressive strength at a later age, the effective retention percentages were (97, 93.5, 96 and 92) for iron, zinc, manganese and chromium ions, respectively, which exceeded 3000 mg/kg initially. The high effectiveness in holding and retaining metals within the matrix of solidification/stabilization at the particle size above 9.5 mm was found as well. The samples (Mn and Cr) with the low amount of cement in the mix treatment were not able to retain the required TCLP regulatory limits value, and the initial extraction pH 4.9. However, the final pH 9.5 is alkanet and stabilization effects of the cement matrix.
- Źródło:
-
Journal of Ecological Engineering; 2019, 20, 3; 91-100
2299-8993 - Pojawia się w:
- Journal of Ecological Engineering
- Dostawca treści:
- Biblioteka Nauki
Artykuł