Tytuł:: The Mechanical Properties and Wear Resistance of HVOF Sprayed WC-Co Coatings
Autorzy:: Özbek, Y.
Canikoğlu, N.
İpek, M.
Powiązania:: https://bibliotekanauki.pl/articles/1187418.pdf
Data publikacji:: 2016-04
Wydawca:: Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:: 81.15.Rs
Opis:: In this work, the Woka 5810 powders (88% tungsten carbide-12% cobalt) were used to produce coating by high velocity oxy-fuel spraying. WC-Co is widely used as a tribological coating material providing a combination of high toughness, high hardness, and good strength. The treated samples were characterized by using optical micrograph, stereo microscope and scanning electron microscopy, X-ray diffractometry, and microhardness tests. Also the wear performance of the coatings was investigated. The results indicated that the coating shows slight higher microhardness and better abrasive wear resistance than the conventional counterpart. The friction coefficient of coating was low. The scanning electron microscopy and energy dispersive spectroscopy analyses were applied to worn surfaces.
Źródło:: Acta Physica Polonica A; 2016, 129, 4; 600-603
0587-4246
1898-794X
Pojawia się w:: Acta Physica Polonica A
Dostawca treści:: Biblioteka Nauki

Artykuł

Skocz do pozycji: 2.

Tytuł:: The Surface Properties of WC-Co-Cr Based Coatings Deposited by High Velocity Oxygen Fuel Spraying
Autorzy:: Ozbek, Y.
Canikoğlu, N.
İpek, M.
Powiązania:: https://bibliotekanauki.pl/articles/1032535.pdf
Data publikacji:: 2017-01
Wydawca:: Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:: 81.15.Rs
Opis:: The aim of this research was to investigate microstructural and mechanical properties of the WC-Co-Cr coatings by high velocity oxygen fuel spraying. Woka 3653 (WC10Co4Cr) powder was used as coating material. This powder is widely used as a tribological coating material providing a combination of high toughness, high hardness, and good strength. The coatings were produced for the different high velocity oxygen fuel spraying parameters. The treated samples were characterized by using scanning electron microscopy/energy dispersive X-ray spectrometry and X-ray diffractometry. Microhardness measurements were executed to evaluate the mechanical properties of the coatings. Also the wear performance of the coatings was investigated. The scanning electron microscopy and energy dispersive X-ray spectrometry analyses were applied to worn surfaces. The results indicated that the coating shows slightly higher microhardness and better abrasive wear resistance than the conventional counterpart.
Źródło:: Acta Physica Polonica A; 2017, 131, 1; 186-189
0587-4246
1898-794X
Pojawia się w:: Acta Physica Polonica A
Dostawca treści:: Biblioteka Nauki

Artykuł

Skocz do pozycji: 3.

Tytuł:: Pack Siliconizing of Ti6Al4V Alloy
Autorzy:: Celebi Efe, G.
İpek, M.
Bindal, C.
Zeytin, S.
Powiązania:: https://bibliotekanauki.pl/articles/1031464.pdf
Data publikacji:: 2017-09
Wydawca:: Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:: 81.65.Lp
81.65.-b
Opis:: In this study, it was aimed to produce titanium silicide layer on Ti6Al4V by a simple, cheap and efficient method of pack siliconizing. Siliconizing was performed in a pack containing a mixture composed of SiO₂ powder as siliconizing source, pure Al powder as a reducer for siliconizing, NH₄Cl as an activator and Al₂O₃ powder as filler, at 1000°C for 8, 10 and 12 hours in open atmospheric furnace. Optical microscope and SEM-EDS studies indicate that the morphology of silicide layers has smooth, dense and layered nature. The presence of phases, confirmed by XRD analyses, reveals that the silicide layers formed at 1000°C are composed of TiSi₂, Ti₃Si₅, TiN, TiO₂ and SiO₂ compounds. Silicide layer thickness was increased with increasing process time and ranged from 7.5 to 9.0 μm. Hardness of silicide layers, measured by Vickers indentation, is over 2100 HV.
Źródło:: Acta Physica Polonica A; 2017, 132, 3; 760-762
0587-4246
1898-794X
Pojawia się w:: Acta Physica Polonica A
Dostawca treści:: Biblioteka Nauki

Artykuł

Informacja