- Aggregate Type Influence on Microstructural Behavior of Concrete Exposed to Elevated Temperature
- Autorzy:
-
Belkadi, Ahmed Abderraouf
Kessal, Oussama
Bensalem, Sara
Aggoun, Salima
Amouri, Chahinez
Khouadjia, Mohamed Lyes Kamel - Powiązania:
- https://bibliotekanauki.pl/articles/27314710.pdf
- Data publikacji:
- 2022
- Wydawca:
- Uniwersytet Zielonogórski. Oficyna Wydawnicza
- Tematy:
-
types of aggregates
high temperature
compressive strength
microstructure
mercury porosimeter
kruszywo
temperatura wysoka
wytrzymałość na ściskanie
mikrostruktura
porozymetr rtęciowy - Opis:
- Exposure of concrete to high temperatures affects its mechanical properties by reducing the compressive strength, bending… etc. Factors reducing these properties have been focused on by several studies over the years, producing conflicting results. This article interested an important factor, that is the type of aggregates. For this, an experimental study on the behavior of concrete based on different types of aggregates: calcareous, siliceous and silico-calcareous subjected to high temperatures. In addition, the particle size distribution of the aggregates was chosen to be almost identical so that the latter does not affect the behavior of the concrete. Aggregates and concrete samples were subjected to a heating/cooling cycle of 300, 600 and 800°C at a speed of 1°C/ min. The mechanical and physical properties of concrete before and after exposure to high temperatures were studied. In addition, a microstructural study using a scanning electron microscope and a mercury porosimeter was performed. Thus, a comparative study between various researches on the mechanical properties of concrete exposed to high temperatures containing different types of aggregates was carried out. The compressive strength test results showed that the concrete based on siliceous aggregates (C-S) has better mechanical performance up to 300°C. However, above 300°C, the compressive strength decreases faster compared to calcareous-based concrete (C-C). According to the mercury porosimeter test, at 600°C, C-SC and C-S concretes have the highest number of pores compared to C-C concretes. The microstructure of concrete at high temperatures was influenced mainly by the aggregate’s types and the paste-aggregate transition zone. This study reinforces the importance of standardizing test procedures related to the properties of concrete in a fire situation so that all the results obtained are reproducible and applicable in other research.
- Źródło:
-
Civil and Environmental Engineering Reports; 2022, 32, 1; 19--42
2080-5187
2450-8594 - Pojawia się w:
- Civil and Environmental Engineering Reports
- Dostawca treści:
- Biblioteka Nauki
Artykuł