- Tytuł:
- Application of DSC Method in Studies on Phase Transitions of Ni Superalloys
- Autorzy:
-
Przeliorz, R.
Piątkowski, J. - Powiązania:
- https://bibliotekanauki.pl/articles/382295.pdf
- Data publikacji:
- 2017
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
innovative material
innovative technology
nickel superalloy
differential scanning calorimetry
specific heat
innowacyjny materiał
technologia innowacyjna
nadstop niklu
skaningowa kalorymetria różnicowa
ciepło właściwe - Opis:
- The paper presents results of calorimetric studies of foundry nickel superalloys: IN100, IN713C, Mar-M247 and ŻS6U. Particular attention was paid to determination of phase transitions temperatures during heating and cooling. The samples were heated to a temperature of 1500°C with a rate of 10°C min–1 and then held at this temperature for 5 min. After a complete melting, the samples were cooled with the same rate. Argon with a purity of 99.99% constituted the protective atmosphere. The sample was placed in an alundum crucible with a capacity of 0.45 cm3. Temperature and heat calibration was carried out based on the melting point of high-purity Ni. The tests were carried out by the differential scanning calorimetry (DSC) using a Multi HTC high-temperature calorimeter from Setaram. Based on the DSC curves, the following temperatures were determined: solidus and liquidus, dissolution and precipitation of the γ’ phase, MC carbides and melting of the γ’/γ eutectic. In the temperature range of 100-1100°C, specific heat capacity of the investigated superalloys was determined. It was found that the IN713C and IN100 alloys exhibit a higher specific heat while compared to the Mar-M247 and ŻS6U alloys.