Temat: austenite transformation - Katalog OPAC zbiorów

Skocz do pozycji: 1.

Tytuł:: Mathematical Model of Bainitic Transformation in Austempered Ductile Iron
Autorzy:: Olejarczyk-Wożeńska, I.
Adrian, H.
Mrzygłód, B.
Głowacki, M.
Powiązania:: https://bibliotekanauki.pl/articles/380252.pdf
Data publikacji:: 2017
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: phase transformations modelling
austenite ferrite transformation
ADI cast iron
TTT diagram
przemiany fazowe
transformacja austenityczna
żeliwo ADI
diagram TTT
Opis:: A mathematical model of austenite - bainite transformation in austempered ductile cast iron has been presented. The model is based on a model developed by Bhadeshia [1, 2] for modelling the bainitic transformation in high-silicon steels with inhibited carbide precipitation. A computer program has been developed that calculates the incubation time, the transformation time at a preset temperature, the TTT diagram and carbon content in unreacted austenite as a function of temperature. Additionally, the program has been provided with a module calculating the free energy of austenite and ferrite as well as the maximum driving force of transformation. Model validation was based on the experimental research and literature data. Experimental studies included the determination of austenite grain size, plotting the TTT diagram and analysis of the effect of heat treatment parameters on the microstructure of ductile iron. The obtained results show a relatively good compatibility between the theoretical calculations and experimental studies. Using the developed program it was possible to examine the effect of austenite grain size on the rate of transformation.
Źródło:: Archives of Foundry Engineering; 2017, 17, 4; 200-206
1897-3310
2299-2944
Pojawia się w:: Archives of Foundry Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Formation of Medium Carbon TRIP Steel Microstructure During Annealing in the Intercritical Temperature Range
Kształtowanie mikrostruktury średniowęglowej stali typu TRIP podczas wyżarzania w zakresie temperatur krytycznych
Autorzy:: Kokosza, A.
Pacyna, J.
Powiązania:: https://bibliotekanauki.pl/articles/354719.pdf
Data publikacji:: 2014
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: phase transformation
critical temperatures
retained austenite
TRIP steels
przemiany fazowe
temperatury krytyczne
austenit szczątkowy
stale TRIP
Opis:: The paper presents the results of research conducted on austenite formation in the microstructure of 41MnSi6-5 TRIP steel during annealing in the intercritical temperature range. The influence of the annealing temperature on the volume fraction of retained austenite in the microstructure of the investigated steel after water quenching was also determined. Based on the results of a dilatometric analysis and metallographic investigation it was noted that the pearlite-to-austenite transformation does not occur at a constant temperature, which is referred to as Ac₁, but rather within some, possible to determine, temperature range which is bounded by the values Ac_1s and Ac_1f. Moreover, through X-ray analysis, it was stated that the largest amount of retained austenite remained in the samples which were annealed at the lowest temperatures in the Ac_1s and Ac_1f range prior to quenching. Increasing the annealing temperature to a two-phase a+g (ferrite + austenite) range, resulted in a decrease of the volume fraction of retained austenite. It was also found that during annealing in Ac_1s and Ac_1f temperature range, austenite is also formed from ferrite simultaneously. This could be the reason for the decrease the carbon content in the formed austenite and consequently the decrease in the volume fraction of retained austenite in the microstructure of the investigated steel, which was quenched after having reached temperatures higher than Ac_1s + 30°C.
W pracy przedstawiono wyniki badań nad tworzeniem się austenitu w mikrostrukturze stali 41MnSi6-5 typu TRIP podczas wyżarzania w zakresie temperatur krytycznych. Określono również wpływ temperatury takiego wyżarzania na udział objętościowy austenitu szczątkowego, jaki pozostaje w mikrostrukturze badanej stali po zahartowaniu od takich temperatur. Na podstawie wyników analizy dylatometrycznej oraz badań metalograficznych stwierdzono, że w badanej stali przemiana perlit – austenit nie przebiega w stałej temperaturze określanej jako Ac_1s lecz w pewnym, możliwym do określenia jej zakresie, którego granice wyznaczają wartości Ac_1s and Ac_1f. Ponadto, metodą analizy rentgenowskiej wykazano, że najwięcej austenitu szczątkowego pozostawało w tych próbkach z badanej stali, które przed zahartowaniem były wyżarzane przy najniższej temperaturze z zakresu Ac_1s and Ac_1f. Podwyższenie temperatury wyżarzania do zakresu dwufazowego a+g (ferryt+ austenit) było przyczyną zmniejszenia udziału austenitu szczątkowego. Stwierdzono, że podczas wyżarzania w zakresie temperatur Ac_1s and Ac_1f tworzy się również z ferrytu. Mogło to być przyczyną zmniejszenia zawartości węgla w tworzącym się austenicie i spadku udziału austenitu szczątkowego w mikrostrukturze badanej stali po jej zahartowaniu od temperatur wyższych od Ac_1s + 30°C.
Źródło:: Archives of Metallurgy and Materials; 2014, 59, 3; 1017-1022
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "austenite transformation" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język