- Tytuł:
- Effect of Cr, Mo and Al on Structure and Selected Mechanical Properties of Austenitic Cast Iron
- Autorzy:
-
Medyński, D.
Janus, A. - Powiązania:
- https://bibliotekanauki.pl/articles/383202.pdf
- Data publikacji:
- 2019
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
austenitic cast iron
austenite transformation
heat treatment
cast
mechanical properties of cast
nickel equivalent
żeliwo austenityczne
zmiana właściwości
obróbka cieplna
odlew
właściwości mechaniczne odlewu - Opis:
- Results of a research on influence of chromium, molybdenum and aluminium on structure and selected mechanical properties of Ni-Mn- Cu cast iron in the as-cast and heat-treated conditions are presented. All raw castings showed austenitic matrix with relatively low hardness, making the material machinable. Additions of chromium and molybdenum resulted in higher inclination to hard spots. However, a small addition of aluminium slightly limited this tendency. Heat treatment consisting in soaking the castings at 500 °C for 4 h resulted in partial transformation of austenite to acicular, carbon-supersaturated ferrite, similar to the bainitic ferrite. A degree of this transformation depended not only on the nickel equivalent value (its lower value resulted in higher transformation degree), but also on concentrations of Cr and Mo (transformation degree increased with increasing total concentration of both elements). The castings with the highest hard spots degree showed the highest hardness, while hardness increase, caused by heat treatment, was the largest in the castings with the highest austenite transformation degree. Addition of Cr and Mo resulted in lower thermodynamic stability of austenite, so it appeared a favourable solution. For this reason, the castings containing the highest total amount of Cr and Mo with an addition of 0.4% Al (to reduce hard spots tendency) showed the highest tensile strength.