Tytuł:: Microstructure and Mechanical Properties of Al-3 Vol% CNT Nanocomposites Processed by High-Pressure Torsion
Autorzy:: Asgharzadeh, H.
Kim, H. S.
Powiązania:: https://bibliotekanauki.pl/articles/354004.pdf
Data publikacji:: 2017
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: high-pressure torsion
aluminum
CNT
microstructure
mechanical properties
Opis:: Al-3 vol% CNT nanocomposites were processed by high-pressure torsion (HPT) at room temperature under the pressure in the range of 2.5-10 GPa for up to 10 turns. Optical microscopy, scanning electron microscopy, and transmission electron microscopy (TEM) were used to investigate the microstructural evolutions upon HPT. Mechanical properties of the HPT-processed disks were studied using tensile tests and microhardness measurements. The results show gradual evolutions in the density, microstructure, and hardness with increasing the number of turns and applied presure. Nanostructured and elongated Al grains with an average grain thickness of ~40 nm perpendicular to the compression axis of HPT and an aspect ratio of ~3 are formed after 10 turns under 6 GPa. Evaluating the mechanical properties of the 10-turn processed Al/CNT nanocomposites indicates a tensile strength of 321 MPa and a hardness of 122 Hv. The tensile fracture surface of the Al/CNT nanocomposite mostly demonstrates a smooth fracture manner with fine dimples resulting in a low tensile ductility of ~1.5%.
Źródło:: Archives of Metallurgy and Materials; 2017, 62, 2B; 1109-1112
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: TEM Study of Recrystallization in Ultra-Fine Grain AA3104 Alloy Processed by High-Pressure Torsion
Analiza procesu rekrystalizacji w stopie AA3104 przetwarzanym w procesie HPT z wykorzystaniem technik transmisyjnej mikroskopii elektronowej
Autorzy:: Paul, H.
Morawiec, A.
Baudin, T.
Czeppe, T.
Powiązania:: https://bibliotekanauki.pl/articles/354358.pdf
Data publikacji:: 2015
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: high pressure torsion
AA3104 alloy
TEM orientation mapping
texture
microstructure
skręcanie pod wysokim ciśnieniem (HPT)
stop AA3104
TEM
tekstura
mikrostruktura
Opis:: The effect of annealing on the microstructure and the texture development was investigated in a particle containing AA3104 aluminium alloy. The samples were processed at room temperature by high-pressure torsion (HPT) up to ten turns. The nucleation of new grains was analyzed by a transmission electron microscope equipped with a system for local orientation measurements and a heating holder. The shear deformation induces a decrease of the grain size. After the first two turns of the HPT processing the initial structure of large grains was ‘transformed’ into a structure of fine cells/grains with the diameter of a few tens of nanometers. In the central areas of the samples the elongated shape of the cells/grains was observed up to six turns. For higher deformations, this structural inhomogeneity was totally removed and only the equiaxed grains were observed. The crystal lattice of small grains rotates in such a way that the <111> direction is parallel to the compression axis. After annealing the structure coarsened. Nevertheless, after primary recrystallization, the structure was still composed of relatively fine and equiaxed grains of a similar size. In most of the observed cases the size of the recrystallized grains in the areas close to and far from the large second phase particles was similar. The recrystallization leads to the creation of new texture components. The new grain orientations lost the positions typically observed in the deformed state and showed the tendency for the coincidence of the <100> crystallographic directions with the compression axis.
W pracy analizowano wpływ warunków wyżarzania na zmiany mikrostrukturalne i teksturowe w stopie AA3104 zawierającym wydzielenia cząstek drugiej fazy. Próbki odkształcano z wykorzystaniem techniki skręcania pod wysokim ciśnieniem (HPT), do dziesięciu obrotów, w temperaturze otoczenia. Proces zarodkowania nowych ziaren analizowano z wykorzystaniem transmisyjnej mikroskopii elektronowej wyposażonej w system pomiaru orientacji lokalnych oraz ‘heating holder’. Zaobserwowano, że w miarę wzrostu liczby obrotów, intensywne ścinanie prowadzi do silnego zmniejszenia wielkości ziarna. Po dwu obrotach, wyjściowa struktura dużych ziaren uległa przekształceniu w strukturę drobnoziarnistą złożoną z ziaren o wielkości kilkudziesięciu nanometrów. W obszarach próbki zbliżonych do osi obrotu wydłużony kształt ziaren obserwowano do sześciu obrotów. W zakresie wyższych stopni odkształcenia ta niejednorodność strukturalna zanika; obserwowano jedynie równoosiowe ziarna. Orientacja sieci krystalicznej tych ziaren formuje silną teksturę osiową z kierunkiem <111> usytuowanym równolegle do kierunku normalnego (osi ściskania/skręcania). Po wyżarzaniu struktura ulega ‘pogrubieniu’. Jednakże, w zakresie rekrystalizacji pierwotnej, w dalszym ciągu pozostaje równoosiowa i silnie rozdrobniona. W większości obserwowanych przypadków wielkość zrekrystalizowanych ziaren w obszarach położonych zarówno w pobliżu, jak i w znacznej odległości od dużych wydzieleń cząstek drugiej fazy, była na zbliżonym poziomie. Proces wyżarzania prowadzi do pojawienia się nowych składowych tekstury. Orientacje nowych ziaren są odmienne od tych, jakie obserwowano w stanie zdeformowanym i wykazują silną tendencję do sytuowania kierunku <100> równolegle do osi ściskania/skręcania.
Źródło:: Archives of Metallurgy and Materials; 2015, 60, 1; 131-144
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "high-pressure torsion" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język