Tytuł:: Mechanical properties of 5083, 5059 and 7020 aluminium alloys and their joints welded by MIG
Autorzy:: Dudzik, K.
Powiązania:: https://bibliotekanauki.pl/articles/245438.pdf
Data publikacji:: 2011
Wydawca:: Instytut Techniczny Wojsk Lotniczych
Tematy:: welding MIG
aluminum alloys
mechanical properties
Opis:: The article presents the research results on the mechanical properties of aluminum alloy 7020 and its MIG welded joints. For comparison alloy 5083 - the most currently used in shipbuilding alloy was chosen as well as 5059 -the new high-strength alloy. Besides the native material alloys there were investigated their joints welded by MIG -the same method as alloy 7020. Welding parameters used for the connection of the sheets made of 7020, 5083 and 5059 alloys were presented. Metallographic analysis showed the correct construction of structural bonded joints. The arc welding method - MIG is the most common method of joining aluminum alloys used in shipbuilding. It replaces the TIG method of providing equally high quality of joints with a much higher performance. The research was carried out using a static tensile test in accordance with the requirements of the Polish Standard PN-EN 10002:2004. Flat samples cut perpendicular to the direction of rolling were used. The research was conducted at the temperature of + 20 centigrade. The 7020 alloy has higher strength properties then alloys: 5083 and 5059. The yield stress is higher by 14.8% compared to 5083 alloy, and by 11.7% compared to the alloy 5059. Plastic properties of an alloy 7020 are the lowest, but with reserves meet the requirements of classification societies. The joints welded by MIG of 7020 alloy have higher strength properties then joints of alloys: 5083 and 5059. Plastic properties of alloy 7020 compared to 5083 alloy are smaller and at the same level as the connector alloy 5059.
Źródło:: Journal of KONES; 2011, 18, 3; 73-77
1231-4005
2354-0133
Pojawia się w:: Journal of KONES
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Joint Formation and Mechanical Properties of 2060 Aluminum Alloy Refill Friction Stir Spot Welding Joint
Autorzy:: Shang, Zhen
Zuo, Yingying
Ji, Shude
Wang, Yue
Chai, Peng
Powiązania:: https://bibliotekanauki.pl/articles/2049424.pdf
Data publikacji:: 2021
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: refill friction stir spot welding
2060 aluminum alloys
plunge depth
defect characteristics
mechanical properties
Opis:: Refill friction stir spot welding (RFSSW) was used to weld the 2060 aluminum alloy with 2 mm thickness. Joint formation, defect characteristics and mechanical properties were investigated. Results show that stir zone (SZ) is clarified into dynamic recrystallization zone (DRZ) and heat extruded zone (HEZ) due to different microstructural features. The size of void near the hook tip decreases with the increase of the plunge depth. Different hook morphologies are obtained under different plunge depths. The tensile-shear load of joint with the void defect initially decreases and then increases with increasing plunge depth. The mean loads of joints under different plunge depths are in the range of 5.1-5.8 kN. The void separates the hook from lap interface, so the cracks initiating from the hook propagate along the sleeve retreating path. The hook has a larger influence on the tensile-shear load of joint than void. All the tensile specimens present a shear-plug fracture mode.
Źródło:: Archives of Metallurgy and Materials; 2021, 66, 1; 153-161
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 3.

Tytuł:: Features of 2017A and AlSi9Mg aluminum alloys friction stir welded with root-side heating
Właściwości stopów 2017A i AlSi9Mg zgrzewanych metodą friction stir welding z podgrzewaniem grani zgrzeiny
Autorzy:: Mroczka, K.
Pietras, A.
Jura, J.
Powiązania:: https://bibliotekanauki.pl/articles/263855.pdf
Data publikacji:: 2016
Wydawca:: Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
Tematy:: aluminum alloys
friction stir welding
heating
structure
mechanical properties
stopy aluminium
nagrzewanie
struktura
właściwości mechaniczne
Opis:: Aluminum alloys 2017A and AlSi9Mg (hypo-eutectic silumin) were friction stir welded with a relatively high linear velocity (over 1 m/min) and use of an additional heat source from the root side of the weld. Macrostructure investigation (with high-resolution images) showed no effect of heating on weld quality. The welding process caused significant fragmentation of the secondary phases in the AlSi9Mg alloy. Furthermore, it was proven that the material above the weld nugget was not mixed and contained micro-defects that were not caused by welding. Also, it contained cavities on the boundaries between Si-particles and the matrix. Based on hardness distribution, a slight strengthening of the cast alloy was observed at the bottom and middle parts of the weld. However, the hardness of the 2017A alloy initially decreased and then increased due to natural aging. This means that the FSW process produced a metastable state in the alloy.
Stop aluminium 2017A i podeutektyczny silumin AlSi9Mg zgrzewano, stosując metodę friction stir welding (FSW). Zastosowano dużą prędkość liniową, powyżej 1 m/min, oraz dodatkowe podgrzewanie grani zgrzeiny. Badania makrostruktury wykazały brak wpływu podgrzewania na jakość złącza. Proces zgrzewania spowodował znaczną fragmentację faz występujących w stopie AlSi9Mg. Ponadto udowodniono, że materiał występujący powyżej jądra zgrzeiny nie jest mieszany i może zawierać mikrodefekty, które nie powstały w wyniku zgrzewania. Zaobserwowano również nieciągłości na granicach cząstek Si/osnowa. Na podstawie rozkładu twardości stwierdzono niewielkie umocnienie stopu odlewniczego pośrodku dolnej części zgrzeiny. Natomiast twardość stopu 2017A najpierw zmalała, a następnie wzrosła w wyniku starzenia naturalnego. To oznacza, że proces zgrzewania wytworzył metastabilny stan tego stopu.
Źródło:: Metallurgy and Foundry Engineering; 2016, 42, 2; 105-115
1230-2325
2300-8377
Pojawia się w:: Metallurgy and Foundry Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 4.

Tytuł:: Mechanical and microstructural properties of EN AW-6060 aluminum alloy joints produced by friction stir welding
Autorzy:: Küçükrendeci, I.
Powiązania:: https://bibliotekanauki.pl/articles/202032.pdf
Data publikacji:: 2015
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: friction stir welding
microstructure
mechanical properties
aluminum alloys
spawanie
tarcie
mikrostruktury
właściwości mechaniczne
stopy aluminium
Opis:: In the study, the mechanical and microstructural properties of friction stir welded EN AW-6060 Aluminum Alloy plates were investigated. The friction stir welding (FSW) was conducted at tool rotational speeds of 900, 1250, and 1500 rpm and at welding speeds of 100, 150 and 180 mm/min. The effect of the tool rotational and welding speeds such properties was studied. The mechanical properties of the joints were evaluated by means of micro-hardness (HV) and tensile tests at room temperature. The tensile properties of the friction stir welded tensile specimens depend significantly on both the tool rotational and welding speeds. The microstructural evolution of the weld zone was analysed by optical observations of the weld zones.
Źródło:: Bulletin of the Polish Academy of Sciences. Technical Sciences; 2015, 63, 2; 475-478
0239-7528
Pojawia się w:: Bulletin of the Polish Academy of Sciences. Technical Sciences
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "aluminum alloys welding" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język