Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "Kurzawa, J." wg kryterium: Autor

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-4 z 4
    Tytuł:
    Bending Strength of Composite Materials with EN AC-44200 Matrix Reinforced with Al2O3 Particles
    Autorzy:
    Kurzawa, J.
    Kaczmar, J. W.
    Powiązania:
    https://bibliotekanauki.pl/articles/381132.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    composite materials
    aluminium oxide particles
    bending strength
    materiały kompozytowe
    tlenek glinu
    wytrzymałość na zginanie
    Opis:
    There are presented results of a research on bending strength of aluminum alloy EN AC-44200 based composite materials reinforced with aluminum oxide particles. The composite materials were manufactured by squeeze casting with the liquid EN AC-44200 Al alloy of porous ceramic preforms under pressure of 100 MPa. For reinforcing of the EN AC-44200 matrix alloy, preforms made of Al2O3 particles with porosity 60, 70, 80 and 90% were applied. In relation to unreinforced EN AC-44200 base Al alloy, bending strength of composite materials increased about 10% per each 10 vol.% increase of Al2O3 particles in the matrix. The highest bending strength of over 400 MPa was reached by the materials reinforced with 30 and 40 vol.% of Al2O3 particles. Microscopic observations of fracture surfaces confirm that the particles intensively restrict plastic deformation of the alloy, which contributes to creation of a typically brittle fracture. The particles present on the crack propagation path inhibit development of microcracks initiated during bend tests. Most often, the fracture runs through interfacial matrix-particle boundaries, which is caused by brittle bridges of silica binder, present on these boundaries.
    Źródło:
    Archives of Foundry Engineering; 2015, 15, 1 spec.; 61-64
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Compressive Strength of EN AC-44200 Based Composite Materials Strengthened with alpha-Al2O3 Particles
    Autorzy:
    Kurzawa, A.
    Kaczmar, J. W.
    Powiązania:
    https://bibliotekanauki.pl/articles/381782.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    compressive strength
    composite materials
    aluminium oxide particles
    wytrzymałość na ściskanie
    materiały kompozytowe
    tlenek glinu
    Opis:
    The paper presents results of compressive strength investigations of EN AC-44200 based aluminum alloy composite materials reinforced with aluminum oxide particles at ambient and at temperatures of 100, 200 and 250oC. They were manufactured by squeeze casting of the porous preforms made of α-Al2O3 particles with liquid aluminium alloy EN AC-44200. The composite materials were reinforced with preforms characterized by the porosities of 90, 80, 70 and 60 vol. %, thus the alumina content in the composite materials was 10, 20, 30 and 40 vol.%. The results of the compressive strength of manufactured materials were presented and basing on the microscopic observations the effect of the volume content of strengthening alumina particles on the cracking mechanisms during compression at indicated temperatures were shown and discussed. The highest compressive strength of 470 MPa at ambient temperature showed composite materials strengthened with 40 vol.% of α-Al2O3 particles.
    Źródło:
    Archives of Foundry Engineering; 2017, 17, 2; 43-48
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Bending Strength of EN AC-44200 – Al2O3 Composites at Elevated Temperatures
    Autorzy:
    Kurzawa, A.
    Kaczmar, J. W.
    Powiązania:
    https://bibliotekanauki.pl/articles/382237.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    wytrzymałość
    stop aluminium
    materiały kompozytowe
    tlenek glinu
    bending strength
    aluminium alloy
    composite materials
    aluminium oxide particles
    Opis:
    The paper presents results of bend tests at elevated temperatures of aluminium alloy EN AC-44200 (AlSi12) based composite materials reinforced with aluminium oxide particles. The examined materials were manufactured by squeeze casting. Preforms made of Al2O3 particles, with volumetric fraction 10, 20, 30 and 40 vol.% of particles joined with sodium silicate bridges were used as reinforcement. The preforms were characterised by open porosity ensuring proper infiltration with the EN AC-44200 (AlSi12) liquid alloy. The largest bending strength was found for the materials containing 40 vol.% of reinforcing ceramic particles, tested at ambient temperature. At increased test temperature, bending strength Rg of composites decreased in average by 30 to 50 MPa per 100°C of temperature increase. Temperature increase did not significantly affect cracking of the materials. Cracks propagated mainly along the interfaces particle/matrix, with no effect of the particles falling-out from fracture surfaces. Direction of cracking can be affected by a small number of agglomerations of particles or of non-reacted binder. In the composites, the particles strongly restrict plastic deformation of the alloy, which leads to creation of brittle fractures. At elevated temperatures, however mainly at 200 and 300°C, larger numbers of broken, fragmented particles was observed in the vicinity of cracks. Fragmentation of particles occurred mainly at tensioned side of the bended specimens, in the materials with smaller fraction of Al2O3 reinforcement, i.e. 10 and 20 vol.%.
    Źródło:
    Archives of Foundry Engineering; 2017, 17, 1; 103-108
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Właściwości materiałów kompozytowych na osnowie stopu aluminium EN AW-2024 i miedzi
    The properties of the EN AW-2024 aluminium alloy and copper matrix composite materials
    Autorzy:
    Kurzawa, A.
    Naplocha, K.
    Kaczmar, J. W.
    Powiązania:
    https://bibliotekanauki.pl/articles/195897.pdf
    Data publikacji:
    2018
    Wydawca:
    Politechnika Rzeszowska im. Ignacego Łukasiewicza. Oficyna Wydawnicza
    Tematy:
    materiały kompozytowe
    właściwości mechaniczne
    infiltracja pod ciśnieniem
    composite materials
    mechanical properties
    pressure infiltration
    Opis:
    W pracy zostały przedstawione wyniki badań wpływu umocnienia stopu EN AW-2024 cząstkami ceramicznymi α-Al2O3 oraz miedzi włóknami Saffil na wybrane właściwości mechaniczne. Materiały kompozytowe zostały wytworzone odlewniczą metodą infiltracji pod ciśnieniem preform ceramicznych charakteryzujących się porowatością otwartą. Stabilność termiczną oraz odporność na deformacje preform w trakcie procesu infiltracji zapewniono przez zastosowanie do ich budowy spoiwa krzemionkowego i odpowiedniej obróbki termicznej. W pracy, opierając się na badaniach struktury i analizy powierzchni przełomów badanych po wytrzymałościowych próbach technologicznych, wykazano wpływ umocnienia na mechanikę tworzenia złomu. Przeprowadzone badania wytworzonych materiałów potwierdziły ponadto ich bardzo dobre właściwości mechaniczne oraz eksploatacyjne, takie jak twardość i odporność na ścieranie, co tworzy zakres ich potencjalnych zastosowań w budowie środków transportu naziemnego.
    In this paper investigations of the strengthening effect of α-Al2O3 particles and Saffil alumina fibres on the EN AW-2024 aluminium alloy matrix as well as Cu based composites on selected mechanical properties were presented. The examined composite materials were produced by pressure infiltration of open porosity preforms. Thermal stability and resistance to deformation of the preforms during the infiltration were provided by using a silica binder for reinforcing their structure and appropriate heat treatment. On the basis of microstructure and surface analysis of fractures obtained during strength investigations the effect of reinforcement and crack development were demonstrated. Performed tests of manufactured materials have also confirmed their superior mechanical and service properties, such as hardness and abrasion resistance, which widens the scope of their potential application.
    Źródło:
    Zeszyty Naukowe Politechniki Rzeszowskiej. Mechanika; 2018, z. 90 [298], 3; 335-344
    0209-2689
    2300-5211
    Pojawia się w:
    Zeszyty Naukowe Politechniki Rzeszowskiej. Mechanika
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-4 z 4

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies