- Tytuł:
-
High-temperature oxidation of Fe40Al5Cr0.2TiB intermetallic phase-based alloy depending on its surface condition
Wysokotemperaturowe utlenianie stopu na osnowie fazy międzymetalicznej Fe40Al5Cr0,2TiB w zależności od stanu powierzchni - Autorzy:
- Cebulski, Janusz
- Powiązania:
- https://bibliotekanauki.pl/articles/41156843.pdf
- Data publikacji:
- 2023
- Wydawca:
- Wydawnictwo SIGMA-NOT
- Tematy:
-
FeAl alloys
high-temperature corrosion
scale
Al2O3 oxide
stop FeAl
korozja wysokotemperaturowa
zgorzelina
tlenek Al2O3 - Opis:
-
The influence of an FeAl intermetallic phase-based alloy’s surface condition on the high-temperature corrosion process during annealing in air at 1000°C for 500 h was investigated. The structure of the oxide scale was determined and related to the initial surface condition before the oxidation process. Oxidation was observed using a Hitachi S-4200 scanning electron microscope. X-ray microanalysis of the chemical composition (EDS) was also carried out for all the tested samples after oxidation. The relationship between the structure of the oxide scale layer and the type of surface before oxidation was demonstrated.
W pracy dokonano analizy wpływu stanu powierzchni na przebieg procesu korozji wysokotemperaturowej stopu na osnowie fazy międzymetalicznej FeAl podczas wyżarzania w powietrzu w temperaturze 1000°C przez 500 h. Określono budowę zgorzeliny tlenkowej i odniesiono te dane do stanu powierzchni przed procesem utleniania. Próbki po procesie utleniania obserwowano przy użyciu elektronowego mikroskopu skaningowego Hitachi S-4200. Przeprowadzono również mikroanalizę rentgenowską składu chemicznego (EDS) wszystkich badanych próbek po utlenianiu. Wykazano zależność pomiędzy budową warstwy zgorzeliny tlenkowej a rodzajem powierzchni przed utlenianiem. - Źródło:
-
Ochrona przed Korozją; 2023, 5; 139-142
0473-7733
2449-9501 - Pojawia się w:
- Ochrona przed Korozją
- Dostawca treści:
- Biblioteka Nauki
Artykuł