    Tytuł:
    Effect of Heat Treatment on Machining Properties of the AlSi9Cu3(Fe) Alloy
    Autorzy:
    Wieroński, W.
    Pezda, J.
    Ponikwia, Ł.
    Powiązania:
    https://bibliotekanauki.pl/articles/379474.pdf
    Data publikacji:
    2016
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    silumin
    heat treatment
    machinability
    refining
    mechanical properties
    cutting power
    aluminum alloys
    obróbka cieplna
    obróbka mechaniczna
    rafinacja
    właściwości mechaniczne
    cięcie
    stopy aluminium
    Opis:
    Automation of machining operations, being result of mass volume production of components, imposes more restrictive requirements concerning mechanical properties of starting materials, inclusive of machinability mainly. In stage of preparation of material, the machinability is influenced by such factors as chemical composition, structure, mechanical properties, plastic working and heat treatment, as well as a factors present during machining operations, as machining type, cutting parameters, material and geometry of cutting tools, stiffness of the system: workpiece – machine tool – fixture and cutting tool. In the paper are presented investigations concerning machinability of the EN AC-AlSi9Cu3(Fe) silumin put to refining, modification and heat treatment. As the parameter to describe starting condition of the alloy was used its tensile strength Rm. Measurement of the machining properties of the investigated alloy was performed using a reboring method with measurement of cutting force, cutting torque and cutting power. It has been determined an effect of the starting condition of the alloy on its machining properties in terms of the cutting power, being indication of machinability of the investigated alloy. The best machining properties (minimal cutting power - Pc=48,3W) were obtained for the refined alloy, without heat treatment, for which the tensile strength Rm=250 MPa. The worst machinability (maximal cutting power Pc=89,0W) was obtained for the alloy after refining, solutioning at temperature 510 oC for 1,5 hour and aged for 5 hours at temperature 175 oC. A further investigations should be connected with selection of optimal parameters of solutioning and ageing treatments, and with their effect on the starting condition of the alloy in terms of improvement of both mechanical properties of the alloy and its machining properties, taking into consideration obtained surface roughness.
    Źródło:
    Archives of Foundry Engineering; 2016, 16, 3; 137-140
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Influence of mechanical activation and heat treatment on surface development and oxide layer thickness of Ti6Al4V ELI alloy
    Autorzy:
    Szota, M.
    Łukaszewicz, A.
    Bukowska, A.
    Powiązania:
    https://bibliotekanauki.pl/articles/367022.pdf
    Data publikacji:
    2019
    Wydawca:
    Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
    Tematy:
    surface engineering
    titanium alloys
    heat treatment
    mechanical activation
    inżynieria powierzchni
    stopy tytanu
    obróbka cieplna
    aktywacja mechaniczna
    Opis:
    Purpose: The paper presents the results of mechanical activation of the surface on oxide layer thickness after heat treatment of TU6Al14V ELI alloy. Design/methodology/approach: Specimens were made from 5 mm diameter rod cut into semicircular slices. The samples were mechanically activated throughout mechanical treatment of the surface: one sandblasted with glass beads during 5 minutes and other ground with sandpaper grit 40, 180, 220 and 800 during 7.5 and 15 minutes. Findings: Then microstructure of specimens etched with Kroll solution was observed using an optical microscope and roughness parameters of the surface were measured. Research limitations/implications: Afterwards heat treatment (550°C, 5 hours) was conducted, then roughness parameters and thickness of the oxide layer were measured by means of a scanning microscope. Practical implications: The conducted research showed up that mechanical activation of the surface which cause an increase of surface development results in greater thickness of the oxide layer which is formed during heat treatment. Nevertheless, mechanical activation that results in a decrease of surface development, such as polishing, results in a decrease of oxide layer thickness. Originality/value: The results of the research can be used to obtain the desired thickness of the oxide layer in the production of the elements that require increased wear and corrosion resistance.
    Źródło:
    Journal of Achievements in Materials and Manufacturing Engineering; 2019, 97, 2; 69-76
    1734-8412
    Pojawia się w:
    Journal of Achievements in Materials and Manufacturing Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The possibility to control the thickness of the oxide layer on the titanium Grade 2 by mechanical activation and heat treatment
    Autorzy:
    Szota, M.
    Łukaszewicz, A.
    Machnik, K.
    Powiązania:
    https://bibliotekanauki.pl/articles/366750.pdf
    Data publikacji:
    2020
    Wydawca:
    Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
    Tematy:
    titanium alloys
    oxide layer
    titanium passivation
    surface mechanical activation
    heat treatment
    stopy tytanu
    warstwa tlenkowa
    pasywacja
    mechaniczna aktywacja powierzchni
    obróbka cieplna
    Opis:
    Purpose: The paper presents the results of microstructure, surface development and thickness of the oxide layer on the pure titanium Grade 2 after mechanical activation and heat treatment (550°C/5h). Design/methodology/approach: Studies show that it is possible to control the thickness of the oxide layer by using different materials to change the roughness of surface - mechanical activation before heat treatment. After mechanical activation and heat treatment, the results of the thickness of the oxide layer as well as a level of surface development were obtained, presented and discussed. Findings: The conducted research have proved that mechanical activation of the surface which cause increase of surface development results in greater thickness of oxide layer which is formed during heat treatment. Nevertheless mechanical activation that results in decrease of surface development, such as polishing, results in decrease of oxide layer thickness. Research limitations/implications: The conducted research have showed up that mechanical activation of the surface which cause increase of surface development results in greater thickness of oxide layer which is formed during heat treatment. Nevertheless, mechanical activation that results in decrease of surface development, such as polishing, results in decrease of oxide layer thickness. Practical implications: are possible using similar method for passivation titanium alloys for medical application. Originality/value: The paper presents the possibility of using mechanical preactivation of surface before heat treatment passivation.
    Źródło:
    Journal of Achievements in Materials and Manufacturing Engineering; 2020, 100, 2; 70-77
    1734-8412
    Pojawia się w:
    Journal of Achievements in Materials and Manufacturing Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies