Tytuł:: The Study of Copper Alloy with Graphene Additive via x-Ray Diffraction
Autorzy:: Masri, Mohamad Najmi
Mohammad, M.
Yusoff, Mahani
Mamat, Sarizam
Teo, Pao Ter
Othman, R.
Irfan, Abd Rahim
Singh, Pramod K.
Powiązania:: https://bibliotekanauki.pl/articles/2134097.pdf
Data publikacji:: 2022
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: copper alloy
graphene
powder metallurgy
copper
zinc
Opis:: This study evaluated the effect of milling speed and compaction pressure on the densification and morphology of the CuZn-Gr composite. The composite was prepared by using the powder metallurgy technique. The effect on the microstructural and compaction was determined based on different milling speeds. The different milling speeds involved were 175, 200, 225, and 250 rpm. Meanwhile, the different compaction pressures used in this study were 127, 250, 374, and 500 MPa. The properties of the milled powder gave the result to green density and densification parameters. The XRD pattern of Cu and Zn broadened as milling time increased.
Źródło:: Archives of Metallurgy and Materials; 2022, 67, 3; 1051--1053
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Testing of Sinters Made of Copper Powders Coated with Carbon Structure Containing Graphene
Badania spieków wykonanych z zastosowaniem proszków miedzi pokrytej strukturą węglową zawierającą grafen
Autorzy:: Rajkowski, Kamil
Majewski, Tomasz
Powiązania:: https://bibliotekanauki.pl/articles/1837982.pdf
Data publikacji:: 2021
Wydawca:: Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego
Tematy:: mechanical engineering
material engineering
powder metallurgy
sintered copper
graphene
inżynieria mechaniczna
inżynieria materiałowa
metalurgia proszków
spieki miedzi
grafen
Opis:: This paper presents the results of preliminary tests on specimens made from mixtures of dendritic copper powder (CuE) with the graphene-coated copper powder (CuG) in a range from 20% to 100% (CuG). The properties of the powder mixtures, green compacts and sinters were determined. To study the properties of the powder mixtures, the following tests were carried out: a measurement of the CuG powder grain size after the grinding process, measurements of the bulk density and tap density of the prepared powder mixtures. The porosity of the produced green compacts and the sinters was calculated as well as the densification capabilities of the powder mixtures by die pressing, cold isostatic pressing and sintering in a reducing atmosphere were tested. Moreover, the nature of the porosity formation was analysed using an optical microscope and the Brinell hardness was determined. The measured Brinell hardness was in the range of 17 HB for sinters made from CuG to 34 HB for sinters made from a 20% CuG powder mixture. More than six hundred measurements that were made in this study show that the high CuG content in the powder mixture reduces the hardness of the sinters as well as increase their porosity.
W artykule zostały przedstawione wyniki wstępnych badań próbek wykonanych z mieszanin proszku miedzi dendrytycznej (CuE) z proszkiem miedzi pokrytym strukturą węglową zawierającą grafen (CuG) w przedziale od 20% do 100% (CuG). W ramach badań określone zostały właściwości mieszaniny proszków, wyprasek oraz spieków, składające się na opis badanego materiału. W celu zbadania właściwości mieszanin proszków zostały wykonane następujące badania: pomiar wielkości ziaren proszku CuG po procesie rozdrabniania, pomiar gęstości nasypowej oraz nasypowej z usadem przygotowanych mieszanin. Obliczono porowatość wytworzonych wyprasek, a następnie spieków oraz sprawdzono możliwości zagęszczania się otrzymanych mieszanin poprzez zastosowanie prasowania matrycowego, prasowania izostatycznego na zimno oraz spiekania w atmosferze redukującej. Dokonano również analizy powierzchni wykonanych próbek pod kątem charakteru powstałych porów za pomocą mikroskopu optycznego oraz określono twardość próbek metodą Brinella. Zmierzona twardość próbek mieści się w zakresie od 17HB dla spieków wykonanych wyłącznie z CuG do 34HB dla spieków wykonanych z mieszanki zawierającej 20% CuG. W ramach badań wykonanych zostało ponad sześćset pomiarów, których wyniki pokazują, że duża zawartość CuG w mieszaninie proszkowej zmniejsza twardość otrzymanych z niej spieków oraz zwiększa ich porowatość.
Źródło:: Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa; 2021, 12, 2 (44); 75-90
2081-5891
Pojawia się w:: Problemy Mechatroniki : uzbrojenie, lotnictwo, inżynieria bezpieczeństwa
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "metallurgy of copper" wg kryterium: Wszystkie pola

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język