    Tytuł:
    Investigations of the Sorption Process’ Kinetics of Sand Moulds’ Surface Layers under Conditions of a High Air Humidity
    Autorzy:
    Kaźnica, N.
    Zych, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/381399.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    sand mould
    surface layer
    moisture sorption
    furan moulding sands
    alkyd moulding sands
    water glass
    forma piaskowa
    warstwa powierzchniowa
    sorpcja wilgoci
    furanowa masa formierska
    szkło wodne
    Opis:
    The results of investigations of the sorption process of surface layers of sand moulds under conditions of a high air humidity are presented in the paper. Investigations comprised three kinds of moulding sands with inorganic and organic binders: moulding sand with hydrated sodium silicate with furfuryl resin and with alkyd resin. Tests were performed on the prototype research stand allowing to maintain a constant, high temperature of surroundings (28–33°C) and the relative air humidity (above 95%). The gravimetric method was applied in measurements. The proposed method allows to assess the amount of water which permeates by the area unit of surface layers of sand moulds into their insides. Knowledge of such parameter allows to select the proper storage conditions of casting moulds waiting for being poured with liquid metals. This can limit the occurrence of surface defects which are caused by too high humidity of casting moulds.
    Źródło:
    Archives of Foundry Engineering; 2015, 15, 3 spec.; 29-32
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Procesy pochłaniania wilgoci z otoczenia i wysychania na przykładzie wierzchnich warstw form odlewniczych
    Moisture Sorption and Desorption Processes on the Example of Moulding Sands’ Surface Layers
    Autorzy:
    Kaźnica, N.
    Zych, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/383349.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    forma piaskowa
    warstwa wierzchnia
    masa formierska
    pochłanianie wilgoci
    wysychanie formy
    sand mould
    surface layer
    moulding sand
    moisture absorption
    Opis:
    W pracy przedstawiono wyniki badania procesów: pochłaniania wilgoci z otoczenia oraz wysychania wierzchnich warstw form piaskowych. Badania obejmowały trzy rodzaje mas formierskich – jedną ze spoiwem nieorganicznym (uwodniony krzemian sodu) i dwie ze spoiwami organicznymi (żywica furfurylowa oraz żywica alkidowa). Badania sorpcji prowadzono na prototypowym stanowisku badawczym pozwalającym na utrzymanie stałej, wysokiej temperatury otoczenia (28–33 °C) oraz wilgotności względnej powietrza powyżej 95%. Badania desorpcji prowadzono na analogicznym stanowisku badawczym zapewniającym odpowiednio niższe wartości wilgotności względnej powietrza oraz temperatury. W obu przypadkach wykorzystano metodę grawimetryczną. Na podstawie analizy otrzymanych wyników wykazano, że wierzchnie warstwy form odlewniczych pochłaniają wilgoć z otoczenia z różną intensywnością, uzależnioną między innymi od ich składu. Jednocześnie, wszystkie zawilgocone badane masy poddane procesowi wysychania oddawały wilgoć do otoczenia. Krzywe sorpcji i desorpcji nie pokrywają się. W przypadku desorpcji zawartość końcowa wilgoci w wierzchnich warstwach form odlewniczych jest większa dla wszystkich badanych mas, niezależnie od rodzaju masy formierskiej.
    The results of investigations of the sorption and desorption process of surface layers of sand moulds are presented in the paper. Investigations comprised three kinds of moulding sands with one inorganic binder (hydrated sodium silicate) and two organic binders: (furfuryl resin and alkyd resin). Tests of sorption process were performed on the prototype research stand allowing to maintain a constant, high temperature of surroundings (28–33 °C) and the relative air humidity above 95%. Tests of desorption process were performed on the analogical research stand ensuring lower value of temperature and the air humidity. The gravimetric method was applied in both measurements. On the bases of achieved results it was shown that surface layers of sand moulds absorb water vapour from surroundings with various intensity which is determined of the chemical composition. Simultaneously, all of the moistened moulding sands which were subjected to the drying process were given moisture to the surroundings back. Sorption and desorption processes curves do not coincide. In case of desorption process the moisture content in the surface layers of all the tested moulding sands is higher irrespective of the kind of moulding sand.
    Źródło:
    Archives of Foundry Engineering; 2015, 15, 4 spec.; 63-66
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Gases Emission From Surface Layers of Sand Moulds and Cores Stored Under the Humid Air Conditions
    Autorzy:
    Kaźnica, N.
    Zych, J.
    Mocek, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/381317.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    surface layer
    sand mould
    emission of gases
    high air humidity
    moulding sand
    chemical binder
    warstwa wierzchnia
    forma piaskowa
    emisja gazów
    wysoka wilgotność powietrza
    masa formierska
    spoiwo chemiczne
    Opis:
    A large number of defects of castings made in sand moulds is caused by gases. There are several sources of gases: gases emitted from moulds, cores or protective coatings during pouring and casting solidification; water in moulding sands; moisture adsorbed from surroundings due to atmospheric conditions changes. In investigations of gas volumetric emissions of moulding sands amounts of gases emitted from moulding sand were determined - up to now - in dependence of the applied binders, sand grains, protective coatings or alloys used for moulds pouring. The results of investigating gas volumetric emissions of thin-walled sand cores poured with liquid metal are presented in the hereby paper. They correspond to the surface layer in the mould work part, which is decisive for the surface quality of the obtained castings. In addition, cores were stored under conditions of a high air humidity, where due to large differences in humidity, the moisture - from surroundings - was adsorbed into the surface layer of the sand mould. Due to that, it was possible to asses the influence of the adsorbed moisture on the gas volumetric emission from moulds and cores surface layers by means of the new method of investigating the gas emission kinetics from thin moulding sand layers heated by liquid metal. The results of investigations of kinetics of the gas emission from moulding sands with furan and alkyd resins as well as with hydrated sodium silicate (water glass) are presented. Kinetics of gases emissions from these kinds of moulding sands poured with Al-Si alloy were compared.
    Źródło:
    Archives of Foundry Engineering; 2017, 17, 4; 79-84
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies