- Tytuł:
-
Chemically crosslinked polyethylene foams of limited flammability
Chemicznie sieciowane pianki polietylenowe o ograniczonej palności - Autorzy:
-
Raszkowska-Kaczor, A.
Stasiek, A.
Janczak, K.
Olewnik-Kruszkowska, E. - Powiązania:
- https://bibliotekanauki.pl/articles/946961.pdf
- Data publikacji:
- 2015
- Wydawca:
- Sieć Badawcza Łukasiewicz - Instytut Chemii Przemysłowej
- Tematy:
-
polyethylene foam
chemical crosslinking
foaming
flame retardancy
pianki polietylenowe
sieciowanie chemiczne
spienianie
uniepalnianie - Opis:
-
A method to prepare chemically crosslinked polyethylene foams from a mixture consisting of polyethylene, foaming agent, crosslinking agent, antioxidant and flame retardant was discussed in this paper. The extrusion was carried out using a twin-screw extruder (temperature of barrel zones: 100, 110, 125 and 125 °C). Crosslinking process of the extruded material was performed at 160 °C for 5 min. The polyethylene films were foamed in silicon oil at 225 °C for 2 min. The influence of the content of flame retardant on density, hardness, flammability and tensile strength of the obtained foam was determined.
Omówiono sposób otrzymywania chemicznie sieciowanych pianek polietylenowych z mieszaniny zawierającej polietylen, środek spieniający, środek sieciujący, antyutleniacz oraz środek ograniczający palność. Proces wytłaczania folii prowadzono w wytłaczarce dwuślimakowej (temperatury stref grzejnych cylindra: 100, 110, 125 i 125 °C). Proces sieciowania prowadzono w temperaturze 160°C w ciągu 5 min. Folię poddano procesowi spieniania w oleju silikonowym w temperaturze 225 °C przez 2 min. Zbadano wpływ zawartości środka ograniczającego palność na gęstość, twardość, palność oraz wytrzymałość na rozciąganie otrzymanych pianek polietylenowych. - Źródło:
-
Polimery; 2015, 60, 4; 283-285