    Tytuł:
    Technology and properties PMN-PT-PS-PFN:LI material for multilayer capacitor
    Technologia i właściwości materiału PMN-PT-PS-PFN:Li na kondensatory wielowarstwowe
    Autorzy:
    Niemiec, P.
    Skulski, R.
    Bochenek, D.
    Wawrzała, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/357026.pdf
    Data publikacji:
    2013
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    ferroelectrics
    multilayer capacitors
    PMN-PT ceramic
    relaxor
    ferroelektryki
    kondensatory wielowarstwowe
    PMN-PT-PS-PFN:Li
    Opis:
    In this work it is designed and obtained the multicomponent material with the formula 0.6075PMN-0.2025PT-0.09PS- 0.1PFN:Li (PMN-PT-PS-PFN:Li) for applications in multilayer ceramic capacitors MLCC. Obtaining of PMN-PT-PS-PFN:Li was done by two alternative methods of synthesis. In the first method a PMN-PT-PS-PFN:Li has been obtained from simple compounds (oxides, carbonates), in the second method the complex compounds (MgNb2O6 and FeNbO4) and simple compounds (oxides PbO, TiO2 and carbonate Li2CO3) were used. From synthesized powder of PMN-PT-PS-PFN:Li the ceramic samples were obtained which have next undergone comprehensive investigations. The X-ray investigations, as well as ferroelectric, dielectric and elastic investigations have been made.
    W pracy zaprojektowano i otrzymano wieloskładnikowy materiał o wzorze 0.6075PMN-0.2025PT-0.09PS-0.1PFN:Li (PMN-PT-PS-PFN:Li) dla zastosowań na podłoża do wielowarstwowych kondensatorów MLCC. Otrzymywanie materiału PMN-PT-PS-PFN:Li było prowadzone dwiema metodami syntetyzowania. W pierwszej metodzie do otrzymania PMN-PT-PS- PFN:Li zastosowano syntetyzowanie prostych związków (tlenki, węglany), w drugiej metodzie zastosowano syntetyzowanie złożonych związków (MgNb2O6 i FeNbO4), oraz prostych związków (tlenków PbO, TiO2 i węglanu Li2CO3). Z syntetyzowanego proszku materiału PMN-PT-PS-PFN:Li otrzymano ceramiczne próbki które zostały poddane kompleksowym badaniom. Przeprowadzono badania rentgenowskie, mikrostrukturalne oraz ferroelektrycznych, dielektrycznych i sprężystych właściwości.
    Źródło:
    Archives of Metallurgy and Materials; 2013, 58, 4; 1313-1316
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    PZT-Type Ceramics Doped with Manganese, Antimony, Lanthanum and Tungsten - Technology and Physical Properties
    Autorzy:
    Bochenek, D.
    Niemiec, P.
    Ćwikiel, E.
    Goryczka, T.
    Powiązania:
    https://bibliotekanauki.pl/articles/353398.pdf
    Data publikacji:
    2020
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    PZT type ceramics
    perovskite type materials
    ferroelectrics
    doped
    Opis:
    The work three ceramic compositions based on PbZr0.49 Ti0.51O3 doped with manganese (Mn), antimony (Sb), lanthanum (La) and tungsten (W) were obtained. The introduction of a set of admixtures was aimed at improving the sinterability of ceramic materials and optimizing its electrophysical parameters. Multi-component materials of the PZT-type with a general formula: Pb(PbZr0.49 Ti0.51)0.94 Mn0.021 Sb0.016 LayWz O3 (where y from 0.008 to 0.012 and z from 0.012 to 0.014) were prepared by the conventional mixed oxide method. After mixing and drying the powder mixtures were calcined in air at 850°C for 4 h, while densification of the powders was carried out by the free sintering method at 1150°C for 2 h. The final steps of technology were grinding, polishing, annealing and putting silver paste electrodes onto both surfaces of the samples for electrical testing. XRD, SEM, EDS, dielectric, ferroelectric, piezoelectric properties and DC electrical conductivity of the obtained ceramic compositions were carried out. X-ray tests of the crystal structure conducted at room temperature have shown that all obtained the PZT-type materials were a single phase (perovskite type) without the presence of a foreign phase. Symmetry of the crystal lattice was identified as space group P4mm. Temperature dielectric studies have shown high values of dielectric permittivity and low dielectric loss. The presented physical properties of ceramic samples based on PZT confirm their predisposition for application in modern microelectronic and micromechatronic applications.
    Źródło:
    Archives of Metallurgy and Materials; 2020, 65, 2; 827-837
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Technology and Dielectric Properties of the KNLN Doped with Nd3+ and Pr3+ Ions
    Autorzy:
    Bochenek, D.
    Osińska, K.
    Mankiewicz, M.
    Niemiec, P.
    Dercz, G.
    Powiązania:
    https://bibliotekanauki.pl/articles/352226.pdf
    Data publikacji:
    2020
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    lead free ceramics
    sodium potassium niobate
    ferroelectrics
    doped
    Opis:
    The paper presents the technology and basic properties of three compositions of lead-free ceramics: (i) (K0.44Na0.52Li0.04)NbO3, (ii) (K0.44Na0.52Li0.04)NbO3)NbO3 +0.5%mol Nd2O3 and (iii) (K0.44Na0.52Li0.04)NbO3)NbO2+0.5%mol Pr2O3. Powders of the designed compositions based on KNLN were obtained with the classic ceramic technology, as a result of solid phase synthesis, from a mixture of simple oxides and carbonates. The synthesis of ceramic powders was carried out at Ts = 900°C for ts = 4 h, while compaction by free sintering at Tsint = 1100°C for tsint = 2 h. XRD studies have shown that doping with praseodymium and neodymium promotes the formation of the tetragonal phase in the base composition (K0.44Na0.52Li0.04)NbO3)NbO3 at lower temperatures. On the other hand, microstructural tests have shown that the admixture of neodymium and praseodymium improves the sinterability of ceramic samples during the technological process; however, the ceramic samples still exhibit high porosity.
    Źródło:
    Archives of Metallurgy and Materials; 2020, 65, 3; 1183-1188
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies