Tytuł:: Electroless Deposition of Composite Nickel-Phosphorous Coatings with Diamond Dispersoid
Autorzy:: Petrova, M.
Georgieva, M.
Chakarova, V.
Dobreva, E.
Powiązania:: https://bibliotekanauki.pl/articles/353820.pdf
Data publikacji:: 2016
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: functional composites
electroless coatings
metal-matrix composites
non-metallic substrate
Opis:: The composite Ni-P coating with diamond particles (D) deposited on the flexible substrates of pressed polyethylene terephthalate material (PET) was obtained, to be used in the development of efficient, flexible grinding and polishing tools. The optimal conditions of the hydrodynamic regime, deposition time and temperature were found. The influence of the concentration and size of the D particles (3/7 ÷ 225/300 μm) on the coating thickness and number of co-deposited particles were studied. By Scanning Electron Microscopy (SEM) images were defined the morphology of dispersion coatings and number of co-deposited particles in them, and Energy Dispersive Spectroscopy (EDS/INCA) was used to determine the elemental chemical composition of the composite coatings.
Źródło:: Archives of Metallurgy and Materials; 2016, 61, 2A; 493-498
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Effect of particle size on surface roughness and morphology of heat-treated electroless Ni-YSZ coating
Autorzy:: Bahiyah Baba, N.
Ghazali, A. S.
Azinee, S. N.
Abdul Rahman, A. H.
Sharif, S.
Powiązania:: https://bibliotekanauki.pl/articles/2201055.pdf
Data publikacji:: 2022
Wydawca:: Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
Tematy:: particle size
electroless coatings
Ni-YSZ
heat treatment
surface roughness
surface morphology
wielkość cząstek
powłoka
powlekanie bezprądowe
obróbka cieplna
chropowatość powierzchni
morfologia powierzchni
Opis:: Purpose The paper discusses the surface characterisation of electroless nickel-yttria-stabilised zirconia (Ni-YSZ) coating with varying YSZ particle sizes and undergoes heat treatment at a temperature between 300-400°C for 1-2 hours for wear resistance purposes. This finding will be helpful to the application of Ni-YSZ as an alternative coating for cutting tools. Design/methodology/approach The surface characterisation was analysed using JOEL Scanning Electron Microscope (SEM) coupled with Energy Dispersive X-ray (EDX) JSM 7800F. The crystallographic structure of materials was analysed by X-ray diffraction (XRD) Bruker D8 Advance instrument. The Ni-YSZ coating was deposited using electroless nickel co-deposition of 8YSZ ceramic particles with a nano, mixed and microparticle sizes onto a high-speed steel (HSS) substrate. The coatings were heat treated at temperature 300-400°C and time 1-2 hours. The surface roughness was measured using Mitutoyo surface roughness tester SJ-301. Findings The electroless Ni-YSZ coating deposited has an average thickness of 30 µm. It is found that the coating morphology electroless coating without YSZ particle incorporation (EN) and Ni-YSZ nano (N) is smoother compared to the Ni-YSZ mixed (NM) and Ni-YSZ micro (M). The EDS composition analysis shows the YSZ content in the electroless Ni-YSZ coating for N samples is the lowest, whereas NM samples are the highest. This resulted in the surface roughness behaviour where the mixed-size YSZ particle gives the highest roughness at all temperatures. The XRD analysis shows that heating temperatures above 300°C caused the precipitation of Ni3P crystalline. Research limitations/implications Previous studies in the surface characterisation of electroless nickel composite are scarce; thus, the study has limitations in finding supporting data. Originality/value The surface characterisation especially related to the surface roughness of the electroless nickel, either the Ni-P or composites or alloys are rarely reported. Thus, this study enlightened the effect of particle size on surface roughness and morphology of heat-treated coatings.
Źródło:: Journal of Achievements in Materials and Manufacturing Engineering; 2022, 114, 1; 5--14
1734-8412
Pojawia się w:: Journal of Achievements in Materials and Manufacturing Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "electroless" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język