Temat: EiS - Katalog OPAC zbiorów

Skocz do pozycji: 1.

Tytuł:: EIS research of AW - 7020 alloy joints welded by MIG
Autorzy:: Dudzik, K.
Charchalis, A.
Powiązania:: https://bibliotekanauki.pl/articles/248097.pdf
Data publikacji:: 2012
Wydawca:: Instytut Techniczny Wojsk Lotniczych
Tematy:: electrochemical impedance spectroscopy (EIS)
aluminium alloys
MIG welding
corrosion
Opis:: The results of corrosion properties research of aluminum alloy AW 7020 (AlZn5Mg1) welded by MIG were presented. In the article the parameters for MIG welding of sheets made of AlZn5Mg1 (7020) alloy was presented. Metallographic analysis of bonds showed a proper structural construction MIG welded 7020 aluminum alloy. EIS measurement was performed in three electrode system in artificial seawater (3.5% NaCl). Impedance studies were carried out at the corrosion potential. Changed voltage signal amplitude in the range plus or minus 10 mV and frequency range of changes was as follows: 100 kHz - 0.1 Hz. Atlas 0531 EU and IA potentiostat was used for studies. Model in the form of an electrical equivalent circuit replacement was chosen for the test object. The results of electrochemical impedance spectroscopy are presented graphically in the Nyquist charts matched with the theoretical curve to them and in the form of parameters characterizing the corrosion process. Obtained results were statistically analyzed. Much better resistance to electrochemical corrosion was found for the native material then joint welded by MIG of 7020 aluminum alloy. The most important parameter - charge transfer resistance value of a double layer Rct for sample of native material is higher than for the sample welded by MIG. Original value is received results of the corrosion properties of MIG welded AlZn5Mg1 alloy compared with the native material.
Źródło:: Journal of KONES; 2012, 19, 1; 83-88
1231-4005
2354-0133
Pojawia się w:: Journal of KONES
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Influence of Friction Stir Welding (FSW) on mechanical and corrosion properties of AW-7020M and AW-7020 alloys
Autorzy:: Dudzik, K.
Jurczak, W.
Powiązania:: https://bibliotekanauki.pl/articles/260119.pdf
Data publikacji:: 2016
Wydawca:: Politechnika Gdańska. Wydział Inżynierii Mechanicznej i Okrętownictwa
Tematy:: Al alloys
mechanical properties
electrochemical impedance spectroscopy (EIS)
corrosion
FSW
friction welding
Opis:: Friction welding associated with mixing the weld material (FSW - Friction Stir Welding ) is an alternative to MIG and TIG welding techniques for Al-alloys. This paper presents experimental results obtained from static tension tests on specimens made of AW-7020M and AW-7020 alloys and their joints welded by using FSW method carried out on flat specimens, according to Polish standards : PN-EN ISO 4136:2011 and PN-EN ISO 6892-1:2010. Results of corrosion resistance tests are also presented. The tests were performed by using the electrochemical impedance spectroscopy (EIS). EIS measurement was conducted with the use of three-electrode system in a substitute sea water environment (3,5% NaCl - water solution). The impedance tests were carried out under corrosion potential. Voltage signal amplitude was equal to 10mV, and its frequency range - 100 kHz ÷ 0,1 Hz. Atlas 0531 EU&IA potentiostat was used for the tests. For the tested object an equivalent model was selected in the form of a substitute electric circuit. Results of the impedance spectroscopy tests are presented in the form of parameters which characterize corrosion process, as well as on Nyquist’s graphs together with the best-fit theoretical curve. Analysis of the test results showed that the value of charge transfer resistance through double layer , Rct , for the FSW- welded specimen , was lower than that for the basic material, and that much greater difference was found in the case of AW-7020M alloy. The impedance spectroscopy tests showed that both the FSW-welded joints and basic material of AW-7020M and AW-7020 alloys were characterized by a good resistance against electrochemical corrosion in sea water environment , and that FSW –welded joints revealed a greater corrosion rate. The performed tests and subject-matter literature research indicate that application of FSW method to joining Al-alloys in shipbuilding is rational.
Źródło:: Polish Maritime Research; 2016, 3; 86-90
1233-2585
Pojawia się w:: Polish Maritime Research
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 3.

Tytuł:: Physicochemical and electrochemical properties of AISI 316L stainless steel used for implants in human urinary system
Ocena własności fizykochemicznych i elektrochemicznych stali AISI 316L stosowanej na implanty w urologii
Autorzy:: Walke, W.
Przondziono, J.
Powiązania:: https://bibliotekanauki.pl/articles/351228.pdf
Data publikacji:: 2013
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: AISI 316L stainless steel
electrochemical impedance spectroscopy (EIS)
X-ray photoelectron spectroscopy (XPS)
scanning electron microscopy (SEM)
austenityczna stal nierdzewna AISI 316L
elektrochemiczna spektroskopia impedancyjna EIS
rentgenowska spektroskopia fotoelektronów XPS
skaningowa mikroskopia elektronowa (SEM)
Opis:: The main purpose of this study was to evaluate physicochemical and electrochemical properties of AISI 316L stainless steel with modified surface, used for implants in human urinary system. In order to simulate conditions, which occur in the tissue environment of the urinary system, the test pieces were exposed in a urinary solution at temperature of T=37 ±1ºC, for a period of 30 days. Evaluation of physicochemical properties of biomaterial was made on the basis of surface chemical analysis (XPS). To evaluate the effects which occur on the surface of the examined steel, Electrochemical Impedance Spectroscopy (EIS) method was also employed. Analysis of test results shows favourable influence of the suggested surface treatment of AISI 316L stainless steel. Samples having electrolytically polished and chemically passivated surface featured the best physicochemical and electrochemical characteristics.
Podstawowym kryterium przydatności biomateriału metalowego na implanty urologiczne (stenty urologiczne) jest biokompatybilność. Jest ona w głównej mierze związana z własnościami fizykochemicznymi powierzchni implantu, które powinny być dostosowane do cech środowiska tkanek układu moczowego człowieka. W celu poprawy biokompatybilności stali Cr-Ni-Mo ustalono warunki wytwarzania warstw pasywnych na jej powierzchni. Wytworzenie warstwy pasywnej obejmowało etap polerowania elektrolitycznego i pasywowania. Taki sposób obróbki powierzchniowej zapewnił chropowatość Ra < 0,16 μm wymaganą dla tego rodzaju implantów. W pracy tej szczególną uwagę skoncentrowano na analizie długotrwałego oddziaływania środowiska sztucznego moczu na własności fizykochemiczne wytypowanej stali. Zasadniczym celem pracy była ocena własnosci fizykochemicznych i elektrochemicznych stali AISI 316L o modyfikowanej powierzchni stosowanej na implanty w układzie moczowym człowieka. W celu zasymulowania warunków występujących w środowisku tkankowym układu moczowego próbki poddawano ekspozycji w roztworze sztucznego moczu o temperaturze T=37±1ºC przez okres 30 dni. O przydatności zaproponowanej warstwy pasywnej do uszlachetniania powierzchni stali w znacznym stopniu decyduje jej skład chemiczny. Dlatego w pracy wykonano badania składu chemicznego metodą spektroskopii fotoelektronów (XPS), z użyciem wielofunkcyjnego spektrometru elektronów PHI 5700/660 firmy Physical Electronics, podczas których zidentyfikowano i wyznaczono stężenia atomowe pierwiastków w badanych warstwach pasywnych. Dla próbek przeprowadzono pomiar widma fotoelektronów w szerokim zakresie energii wiązania od 0÷1400 eV oraz dokładne pomiary linii widmowych poszczególnych pierwiastków składowych z warstwy powierzchniowej. Dla oceny zjawisk zachodzacych na powierzchni badanej stali zastosowano również metodę elektrochemicznej spektroskopii impedancyjnej (EIS). Pomiary przeprowadzono z wykorzystaniem systemu pomiarowego AutoLab PGSTAT 302N wyposażonego w moduł FRA2 (Frequency Response Analyser). Badania przeprowadzono w alternatywnym roztworze symulującym środowisko moczu człowieka. Zastosowana w pracy mikroskopia skaningowa pozwoliła na ocene stanu powierzchni stali AISI 316L przed i po ekspozycji w sztucznym moczu. Analiza wyników badań wskazuje na korzystny wpływ zaproponowanej obróbki powierzchniowej stali AISI 316L. Najkorzystniejszą charakterystykę fizykochemiczną i elektrochemiczną miały próbki o powierzchni polerowanej elektrolitycznie i pasywowanej chemicznie. Przeprowadzone w pracy badania stanowią podstawę do dalszych analiz związanych z zagadnieniem biokompatybilności stali Cr-Ni-Mo stosowanej na implanty w urologii.
Źródło:: Archives of Metallurgy and Materials; 2013, 58, 2; 625-630
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "EiS" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język