Tytuł:: Entall - thermodynamic database of alloys
Entall - termodynamiczna baza danych stopów
Autorzy:: Dębski, A.
Powiązania:: https://bibliotekanauki.pl/articles/355184.pdf
Data publikacji:: 2013
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: database
thermodynamic properties
hydrogen storage
bazy danych
właściwości termodynamiczne
magazynowanie wodoru
Opis:: Li-Si, Ag-Ca, B-Li, Ca-Li and Al-Li belong to the group of application alloys. The Entall database includes experimental data on the enthalpy of formation of the intermetallic phases belonging to the mentioned systems, as well as software for the calculation of other thermodynamic functions. The presented Entall database is the first proposal of a thermodynamic property data, which will be gradually extended by new metal alloy systems. It is a free database, available at www.entall.imim.pl.
Stopy Li-Si, Ag-Ca. B-Li, Ca-Li. oraz Al-Li należą do grupy stopów, mających zastosowania aplikacyjne. Baza Entall zawiera eksperymentalne dane entalpii tworzenia faz międzymetalicznych należących do cytowanych układów oraz oprogra- mowanie dające możliwość wyliczenia innych funkcji termodynamicznych. Prezentowana baza Entall jest pierwszą propozycją bazy właściwości termodynamicznych, która będzie stopniowo rozbudowywana o nowe układy stopów metali. Jest to baza darmowa i dostępna pod adresem www.entall.imim.pl.
Źródło:: Archives of Metallurgy and Materials; 2013, 58, 4; 1147-1148
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: New Features of Entall Database: Comparison of Experimental and Model Formation Enthalpies
Nowe funkcje bazy danych Entall: porównanie doświadczalnych i modelowych entalpii tworzenia
Autorzy:: Dębski, A.
Dębski, R.
Gąsior, W.
Powiązania:: https://bibliotekanauki.pl/articles/353128.pdf
Data publikacji:: 2014
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: COST 535
database
thermodynamic properties
Miedema model
baza
właściwości termodynamiczne
model Miedemy
Opis:: This paper presents a new version of the Entall database of the thermodynamic properties of metals and their alloys. The changes are related to the thermodynamic data of new binary and ternary systems as well as the integration of the database with an application for the modeling of the formation enthalpies of intermetallic phases with the use of the Miedema model. Using this tool, calculations of the enthalpies of formation of 38 intermetallic phases from 12 binary systems were performed and a comparative analysis conducted. The results of the analysis clearly showed a weak correlation between the model and experimental data. To improve this correlation, an intermediate method of proportional change was proposed, on the basis of the measurement of the enthalpy of formation for one of the phases. The values for the other phases obtained from this indirect method should not deviate much from the experimental ones provided that before the measurements (dissolving or pulping) or after them (direct synthesis), the phase being examined should undergo structural tests, in order to confirm its dominating amount in the samples.
W pracy przedstawiona została nowa wersja bazy właściwośsci termodynamicznych metali i stopów Entall. Modyfikacja dotyczyła z jednej strony danych termodynamicznych nowych układów dwu i trójskładnikowych a z drugiej zaadaptowania do niej opracowanego programu (kalkulatora) do modelowania entalpii tworzenia faz międzymetalicznych modelem Miedemy. Korzystając z tego nowego narzędzia wykonane zostały obliczenia entalpii tworzenia dla 38 faz międzymetalicznych z 12 układów dwuskładnikowych oraz przeprowadzona została analiza porównawcza. Wyniki analizy pokazały jednoznacznie słaba korelacje między danymi modelowymi i doświadczalnymi. Dla poprawienia tej korelacji zaproponowana została pośrednia metoda proporcjonalnej zmiany w oparciu o pomiar entalpii tworzenia dla jednej z faz. Uzyskane z tej pośredniej metody wartości dla innych faz powinny niewiele odbiegąc od eksperymentalnych przy spełnieniu warunku, że faza dla której wykonywane były badania została przed pomiarami (rozpuszczanie lub roztwarzanie) lub po nich (bezpośrednia synteza) poddana badaniom strukturalnym, w celu potwierdzenia jej dominującej ilości w próbkach.
Źródło:: Archives of Metallurgy and Materials; 2014, 59, 4; 1337-1343
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "właściwości termodynamiczne" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język