Prediction of transport vehicles’ durability with consideration of corrosive surface cracks propagation in structural elements
Autorzy:
Droździel, P.
Popovych, P.
Vitenko, T.
Shevchuk, O.
Zolotyi, R.
Kononchuk, O.
Powiązania:
https://bibliotekanauki.pl/articles/198683.pdf
Data publikacji:
2018
Wydawca:
Politechnika Śląska. Wydawnictwo Politechniki Śląskiej
Tematy:
structure element
surface cracks
kinetic diagrams
crack propagation
corrosive-fatigue crack
durability of vehicle
element konstrukcji
pęknięcia powierzchni
diagram kinetyczny
propagacja pęknięć
pęknięcia korozyjno-zmęczeniowe
obciążenie pojazdu
Opis:
Support frameworks of transport vehicles operate under varying terrain conditions under the influence of extreme climate and corrosive environments. When transporting cargo, dust is deposited on the surface of metal structures. The combination of dust and moisture creates an aggressive environment resulting in intense corrosion damage. The damage is caused by the defects of corrosion pitting, which occur on the surface and transform into corrosion cracks. Based on energy approaches, with the application of well-known results for the mathematical description of electrochemical reactions and the principles of fragile fracture mechanics, an analytical model of durability is proposed for the first time. The model determines the residual life of maximum loaded elements of undercarriages with surface cracks under the action of dynamic loads and corrosive environments. For this case, a set of mathematical relations in the form of a non-linear differential equation was developed, as well as the initial and final conditions for determining the life of vehicles’ structural elements with corrosive surface cracks. The analytical model implementation is proven by solving the problem of determining the residual life of a vehicle’s element, i.e., a steel plate, weakened by a semi-elliptical surface crack, which is under the action of dynamic loads in a 3% sodium chloride solution. The insignificant increase in the crack’s initial size is proven to greatly reduce the period of its subcritical growth. The developed model was applied to define the residual life of thin-walled elements of structures with surface cracks.
Źródło:
Zeszyty Naukowe. Transport / Politechnika Śląska; 2018, 101; 47-57
0209-3324
2450-1549
Pojawia się w:
Zeszyty Naukowe. Transport / Politechnika Śląska
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies