Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "passivation" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-4 z 4
    Tytuł:
    Characterization of Long-Term Corrosion Performance of Ti15Mo Alloy in Saline Solution
    Autorzy:
    Szklarska, M.
    Łosiewicz, B.
    Dercz, G.
    Zubko, M.
    Albrecht, R.
    Stróż, D.
    Powiązania:
    https://bibliotekanauki.pl/articles/357034.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    biomaterial
    corrosion resistance
    passivation
    structure
    titanium alloys
    Opis:
    The Ti15Mo alloy has been studied towards long-term corrosion performance in saline solution at 37°C using electrochemical impedance spectroscopy. The physical and chemical characterization of the material were also investigated. The as-received Ti15Mo alloy exhibits a single β-phase structure. The thickness of single-layer structured oxide presented on its surface is ~4 nm. Impedance measurements revealed that the Ti15Mo alloy is characterized by spontaneous passivation in the solution containing chloride ions and formation of a double-layer structured oxide composed of a dense interlayer being the barrier layer against corrosion and porous outer layer. The thi ckness of this oxide layer, estimated based on the impedance data increases up to ~6 nm during 78 days of exposure. The obs erved fall in value of the log|Z|f=0.01 Hz indicates a decrease in pitting corrosion resistance of Ti15Mo alloy in saline solution along with the immersion time. The detailed EIS study on the kinetics and mechanism of corrosion process and the capacitive behavior of the Ti15Mo electrode | passive layer | saline solution system was based on the concept of equivalent electrical circuit with respect to the physical meaning of the applied circuit elements. Potentiodynamic studies up to 9 V vs. SCE and SEM analysis show no presence of pitting corrosion what indicates that the Ti15Mo alloy is promising biomaterial to long-term medical applications.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 2; 773-778
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Wpływ pasywacji na odporność korozyjną stopu NiTi
    Influence of passivation on corrosion resistance of NiTi alloy
    Autorzy:
    Kaczmarek, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/284748.pdf
    Data publikacji:
    2010
    Wydawca:
    Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów
    Tematy:
    biomateriały
    stopy z pamięcią kształtu
    odporność korozyjna
    pasywacja
    biomaterials
    shape memory alloys
    corrosion resistance
    passivation
    Opis:
    Celem przeprowadzonych badań było określenie wpływu różnych metod pasywacji powierzchni stopu NiTi na odporność korozyjną. Analizowano dwa warianty pasywacji powierzchni: chemiczną oraz elektrochemiczną. Dla każdego z zaproponowanych wariantów zastosowano różne kąpiele oraz oceniano wpływ parametrów procesów na odporność korozyjną.
    The aim of the research was determination of influence of different passivation methods of NiTi alloy on corrosion resistance. Two variants of passivation were analyzed: chemical and electrochemical. For each of the proposed variant different baths and parameters were applied.
    Źródło:
    Engineering of Biomaterials; 2010, 13, no. 99-101; 32-34
    1429-7248
    Pojawia się w:
    Engineering of Biomaterials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Chemical passivation as a method of improving the electrochemical corrosion resistance of Co-Cr-based dental alloy
    Autorzy:
    Rylska, D.
    Sokołowski, G.
    Łukomska-Szymańska, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/306992.pdf
    Data publikacji:
    2017
    Wydawca:
    Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
    Tematy:
    odporność korozyjna
    stop stomatologiczny
    test elektrochemiczny
    pasywacja chemiczna
    corrosion resistance
    dental alloys
    electrochemical test
    chemical passivation
    Opis:
    Purpose: The purpose of the study was to evaluate corrosion resistance of Wirobond C® alloy after chemical passivation treatment. Methods: The alloy surface undergone chemical passivation treatment in four different media. Corrosion studies were carried out by means of electrochemical methods in saline solution. Corrosion effects were determined using SEM. Results: The greatest increase in the alloy polarization resistance was observed for passive layer produced in Na2SO4 solution with graphite. The same layer caused the highest increase in corrosion current. Generally speaking, the alloy passivation in Na2SO4 solution with graphite caused a substantial improvement of the corrosion resistance. The sample after passivation in Na2SO4 solution without graphite, contrary to others, lost its protective properties along with successive anodic polarization cycles. The alloy passivation in Na3PO4 solution with graphite was the only one that caused a decrease in the alloy corrosion properties. The SEM studies of all samples after chemical passivation revealed no pit corrosion – in contrast to the sample without any modification. Conclusions: Every successive polarization cycle in anodic direction of pure Wirobond C® alloy enhances corrosion resistance shifting corrosion potential in the positive direction and decreasing corrosion current value. The chemical passivation in solutions with low pH values decreases susceptibility to electrochemical corrosion of Co-Cr dental alloy. The best protection against corrosion was obtained after chemical passivation of Wirobond C® in Na2SO4 solution with graphite. Passivation with Na2SO4 in solution of high pH does not cause an increase in corrosion resistance of WIROBOND C. Passivation process increases alloy resistance to pit corrosion.
    Źródło:
    Acta of Bioengineering and Biomechanics; 2017, 19, 2; 73-78
    1509-409X
    2450-6303
    Pojawia się w:
    Acta of Bioengineering and Biomechanics
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Influence of Passivation Type on Corrosion Resistance of Ti15Mo Alloy in Simulated Body Fluids
    Wpływ rodzaju pasywacji powierzchni stopu Ti15Mo na jego odporność korozyjną w środowisku płynów ustrojowych
    Autorzy:
    Szklarska, M.
    Dercz, G.
    Rak, J.
    Łosiewicz, B.
    Simka, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/353709.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    biomaterial
    electrochemical impedance spectroscopy
    corrosion resistance
    passivation
    titanium alloys
    biomateriały
    elektrochemiczna spektroskopia impedancyjna
    odporność na korozję
    pasywacja
    stopy tytanu
    Opis:
    This work reports on determination of the influence of passivation type of Ti15wt.%Mo implant alloy surface on its corrosion resistance in simulated body fluids. The alloy under investigation was subjected to natural self-passivation in air, and forced passivation by autoclaving in steam, boiling in 30 % solution of H2O2, and electrochemical passivation in 0.9 % NaCl solution. Resistance of the passivated Ti15Mo alloy to pitting corrosion was studied at 37ºC in 0.9 % NaCl solution using open circuit potential method, anodic polarization curves, and electrochemical impedance spectroscopy (EIS). Comparative estimation of the determined parameters of corrosion resistance revealed that the obtained passive layers improve anticorrosive properties of the tested alloy. Surface of the alloy subjected to passivation in steam autoclave reveals the highest protection against pitting corrosion. Anodic potentiodynamic curves showed that the Ti15Mo alloy after different passivation types of the surface is characterized by a lack of susceptibility to pitting corrosion up to potential of 9 V. Based on the EIS investigations, the thickness of the formed oxide layers (TiO2, anatase) was determined to be in the range from 2.0 to 7.8 nm in dependence on the applied type of passivation. It was ascertained that electrochemical properties of the Ti15Mo alloy and possibility of its surface passivation using simple methods, make it an attractive material for use in biomedicine for long-term implants.
    Praca dotyczy określenia wpływu rodzaju pasywacji powierzchni stopu Ti15%wag.Mo na jego odporność korozyjną w środowisku płynów ustrojowych. Badany stop poddano naturalnej samopasywacji w powietrzu oraz wymuszonej pasywacji w autoklawie parowym, w gotującym się 30 % roztworze H2O2 oraz elektrochemicznej pasywacji w 0,9 % roztworze NaCl. Odporność pasywowanego stopu Ti15Mo na korozję wżerową badano w temperaturze 37°C w roztworze 0,9 % NaCl metodą potencjału obwodu otwartego, krzywych polaryzacji anodowej oraz elektrochemicznej spektroskopii impedancyjnej (ESI). Ocena porównawcza wyznaczonych parametrów odporności korozyjnej wykazała, że wytworzone warstwy pasywne poprawiają właściwości antykorozyjne badanego stopu. Powierzchnia stopu poddana pasywacji w autoklawie parowym wykazuje najwyższą ochronę przed korozją wżerową. Anodowe krzywe potencjodynamiczne ujawniły, że stop Ti15Mo poddany różnym sposobom pasywacji powierzchni wykazuje brak podatności na korozję wżerową aż do potencjału wynoszącego 9 V. W oparciu o badania ESI wyznaczona została grubość otrzymanych warstw tlenkowych (TiO2, anataz), która w zależności od zastosowanego sposobu pasywacji mieściła się w zakresie od 2,0 do 7,8 nm. Stwierdzono, że właściwości elektrochemiczne stopu Ti15Mo oraz możliwość pasywowania jego powierzchni prostymi metodami, czynią go atrakcyjnym materiałem do zastosowań w biomedycynie na implanty długoterminowe.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 4; 2687-2694
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-4 z 4

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies