Tytuł:
Scale effect of cement mortar specimens subjected to high temperatures using uniaxial compressive and splitting tensile tests
Autorzy:
Xiong, L. X.
Zhang, X. J.
Xu, Z. Y.
Geng, D. X.
Powiązania:
https://bibliotekanauki.pl/articles/230921.pdf
Data publikacji:
2020
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
zaprawa cementowa
temperatura wysoka
ściskanie jednoosiowe
rozciąganie przy rozłupywaniu
efekt skali
cement mortar
high temperature
uniaxial compression
splitting tensile
scale effect
Opis:
In this study, cubic and cylindrical cement mortar specimens were first subjected to high temperatures, then the cubic and cylindrical specimens were taken out and conducted with uniaxial compressive test and splitting tensile test, respectively. The effect of the length to side ratio on the uniaxial compressive properties and the effect of thickness-to-diameter ratio on the splitting tensile properties of cement mortar specimens after high temperature were studied. Test results show that: (1) With temperature increasing from 25 ºC (room temperature) to 400 ºC, the compressive strength and elastic modulus of cubic specimens with three kinds of side lengths decrease; the decreasing rates of compressive strength and elastic modulus of cubic specimen with side length of 70.7 mm is higher than those of cubic specimens with side length of 100 mm and 150 mm, and the strain at the peak stress of cubic specimens with three kinds of side lengths increase. (2) After the same temperature, the tensile strength of cylindrical specimen decreases with the thickness-to-diameter ratio increasing from 0.5 to 1.0. The decreasing rate of tensile strength of cylindrical specimen with thickness-to-diameter ratio is highest when the temperature is 25 ºC (room temperature), followed by that after the temperature of 200 ºC, and that after the temperature of 400 ºC is the lowest.
Źródło:
Archives of Civil Engineering; 2020, 66, 3; 139-155
1230-2945
Pojawia się w:
Archives of Civil Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies