Leaching of High Arsenic Content Dust and a New Process for the Preparation of Copper Arsenate
Autorzy:
Sheng, W.
Shen, Y.-Y.
Sheng-Quan, Z.
Powiązania:
https://bibliotekanauki.pl/articles/355005.pdf
Data publikacji:
2018
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
high-arsenic dust
acidic leaching
alkaline leaching
copper arsenate
comprehensive utilisation of esources
Opis:
In this research, the high arsenic content dust of copper smelting, as a raw material, the extraction of copper and arsenic from the high arsenic content dust in the leaching system containing acidic and alkaline compounds was investigated. Meanwhile, the effects of acid/alkaline initial concentration, liquid to solid ratio, leaching temperature, leaching time on the leaching rate of copper and arsenic were studied. The optimum conditions for the leaching of high arsenic content dust and preparation of copper arsenate were determined. The results showed that acidic/alkaline leaching of high arsenic content dust was particularly effective. 93.2% of the copper, and 91.6% of the arsenic were leached in an acidic leaching process and 95% of the arsenic, while less than 3% of the copper, less than 5% of the antimony, less than 2% of the bismuth was also leached in an alkaline leaching process. A new method (the parallel flow drop precipitate method) was developed in the synthesis of copper arsenate process. The parallel flow drop method was employed to adjust the molar ratio (copper to arsenic) of the mixed solution of the acid-leaching solution and the alkali-leaching solution by taking the drop acceleration of an acidic leaching solution and an alkaline leaching solution at 10 mL/min and 12 mL/min, at a temperature of 60°C and a reaction time of 1h. Copper arsenate was prepared by mixing an acidic leaching solution and an alkaline leaching solution. The main phases of copper arsenate were CuHAsO4·1.5H2O and Cu5As4O15·9H2O. Copper arsenate contained 30.13% copper and 31.10% arsenic.
Źródło:
Archives of Metallurgy and Materials; 2018, 63, 3; 1167-1172
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies