- ZrO2-CeO2 ceramic powders obtained from a sol-gel process using acetylacetone as a chelating agent for potential application in prosthetic dentistry
- Autorzy:
-
Nakonieczny, D.
Paszenda, Z.
Drewniak, S.
Radko, T.
Lis, M. - Powiązania:
- https://bibliotekanauki.pl/articles/306436.pdf
- Data publikacji:
- 2016
- Wydawca:
- Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
- Tematy:
-
proces zol-żel
metody rentgenowskie
analiza termiczna
ZrO2
protetyka
sol-gel process
X-ray Methods
Thermal Analysis
Prosthetic Dentistry - Opis:
- Purpose: The main objective of this study was to obtain single-phase β-ZrO2 powders with so-called soft agglomerates reproducibile morphology with acetyl-acetone as a chelating-agent. To the best of our knowledge there is no avaiable data which determine the effect of acetyl acetone on the phase composition and morphology of ceria-doped ZrO2 powders for biomedical applications. Methods: Twenty variants of powders with different water to zirconia precursor and acetylacetone to zirconia precursor molar ratios were prepared. 0.9ZrO20.1CeO2 powders were obtained by a hydrolysis and condensation and further calcination of zirconium n-propoxide in a simple one-step sol-gel process. Influence of acetyloacetone to zirconia precursor on the phase composition ratio and water to zirconia precursor was investigated. Samples have been characterized by X-ray diffraction (XRD), Raman spectroscopy (RS), thermal analysis (TGA/DTA) and scanning electron microscopy (SEM) measurements. Results: Ceramic powders prepared by sol-gel process, according to the various concentration of chelating agent and water show different morphology and phase composition. Conclusions: Higher molar ratios of AcAc in range with smaller amounts of water cause hard agglomerates, obtained powders are characterized by highly thermally stable behaviour and various phase composition. With higher molar ratios of water to zirconium-n-propoxide so-called soft agglomerates and one phase powders are obtained.
- Źródło:
-
Acta of Bioengineering and Biomechanics; 2016, 18, 3; 53-60
1509-409X
2450-6303 - Pojawia się w:
- Acta of Bioengineering and Biomechanics
- Dostawca treści:
- Biblioteka Nauki
Artykuł