Tytuł:
The effect of the modification by ultrafine silicon carbide powder on the structure and properties of the Al-Si alloy
Autorzy:
Kovbasiuk, T. M.
Selivorstov, V. Yu.
Dotsenko, Yu. V.
Duriagina, Z. A.
Kulyk, V. V.
Kasai, O. M.
Voitovych, V. V.
Powiązania:
https://bibliotekanauki.pl/articles/1818500.pdf
Data publikacji:
2020
Wydawca:
Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
Tematy:
Al-Si alloy
silicon carbide
modification
mechanical properties
microstructure
microhardness
Stop Al-Si
węglik krzemu
modyfikacja
właściwości mechaniczne
mikrostruktura
mikrotwardość
Opis:
Purpose: Determine the possibility of modifying aluminium alloys of the Al-Si system with an ultrafine SiC modifier with a particie size of 3-5 pm. Design/methodology/approach: Processing of the Al-Si alloy was carried out by introducing an ultrafine modifier in the amount of 0.1, 0.2, or 0.3 wt.%. Silicon carbide (SiC) with a particle size in the range of 3-5 pm was used as a modifier. To study the microstructure of the formed surface layers, a metallographic analysis was performed according to the standard method on a microscope MIKPOTEX® MMT-14C using TopView software. Microhardness studies of the samples were carried out on a Vickers microhardness tester NOVOTEST TC-MKV1. The microstructure of castings of the AlSi12 grade was studied at magnification from 100 to 400 times on the horizontal and vertical surfaces of the samples after etching with a 2% NaOH aqueous solution. Findings: Aluminium cast alloy of Al-Si system has been synthesized with the addition of 0.1, 0.2, and 0.3 wt.% ultrafine SiC modifier. It was found that the modification of the AlSi12 alloy by SiC particles of 3-5 pm in size led to an improvement of its microstructure due to the reduction of the volume fraction of micropores and primary Si crystals. It was shown that the AlSi12 aluminium alloy due to the modification by 0.2 wt.% SiC has the best micromechanical properties and macrostructure density. Research limitations/implications: The obtained research results are relevant for cast specimens of the indicated sizes and shapes. The studies did not take into account the influence of the scale factor of the castings. Practical implications: The developed modification technology was recommended for use in the conditions of the foundry "Dnipropetrovsk Aggregate Plant" (Dnipro, Ukraine). Originality/value: The technology of AlSi12 alloy modification of ultrafine SIC modifier with a particle size of 3-5 pm was used for the first time.
Źródło:
Archives of Materials Science and Engineering; 2020, 101, 2; 57--62
1897-2764
Pojawia się w:
Archives of Materials Science and Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies