- Effect of alloying elements on solidification of primary austenite in Ni-Mn-Cu cast iron
- Autorzy:
-
Janus, A.
Kurzawa, A. - Powiązania:
- https://bibliotekanauki.pl/articles/382123.pdf
- Data publikacji:
- 2011
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
primary austenite
solidification process
austenitic cast iron
Ni-Mn-Cu cast iron
austenit pierwotny
proces krzepnięcia
żeliwo austenityczne
żeliwo Ni-Mn-Cu - Opis:
- Within the research, determined were direction and intensity of alloying elements influence on solidification way (directional or volumetric) of primary austenite dendrites in hypoeutectic austenitic cast iron Ni-Mn-Cu. 50 cast shafts dia. 20 mm were analysed. Chemical composition of the alloy was as follows: 1.7 to 3.3 % C, 1.4 to 3.1 % Si, 2.8 to 9.9 % Ni, 0.4 to 7.7 % Mn, 0 to 4.6 % Cu, 0.14 to 0.16 % P and 0.03 to 0.04 % S. The discriminant analysis revealed that carbon influences solidification of primary austenite dendrites most intensively. It clearly increases the tendency to volumetric solidification. Influence of the other elements is much weaker. This means that the solidification way of primary austenite dendrites in hypoeutectic austenitic cast iron Ni-Mn-Cu does not differ from that in an unalloyed cast iron.
- Źródło:
-
Archives of Foundry Engineering; 2011, 11, 2 spec.; 93-96
1897-3310
2299-2944 - Pojawia się w:
- Archives of Foundry Engineering
- Dostawca treści:
- Biblioteka Nauki