    Tytuł:
    Composite zones produced in iron castings by in-situ synthesis of TiC carbides
    Strefy kompozytowe otrzymywane w odlewach z żeliwa w wyniku syntezy in situ węglików TiC
    Autorzy:
    Olejnik, E.
    Górny, M.
    Tokarski, T.
    Grabowska, B.
    Kmita, A.
    Sikora, G.
    Powiązania:
    https://bibliotekanauki.pl/articles/356291.pdf
    Data publikacji:
    2013
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    MMCs
    in situ
    composites zone
    TiC
    castings
    synteza in situ
    strefy kompozytowe
    odlewy
    Opis:
    The study discusses a method of producing composite zones at the edge of castings made of ferritic-pearlitic ductile iron. Composite zones were produced in castings made of ferritic-pearlitic ductile iron at the casting edge. The reinforcing phase for the composite zone was TiC carbide, obtained by in-situ synthesis of substrates introduced into the mould in the form of compacts. The composition of the substrates of the reaction of the TiC synthesis was next enriched with an Fe filler added in an amount of 10 and 50 wt. % to investigate the possibility of changing the hardness of the composite zone. The addition of filler changed the surface fraction and the average size of TiC precipitates. In the case of the 50 wt. % addition, a tenfold reduction in the dimensions of the carbides was obtained. This increased their surface fraction relative to the compact composition containing only 10 wt. % of the filler. Changes in mechanical properties were analysed within the zone area by the measurement of hardness HV. The study showed a gradual decrease of the zone hardness in function of the amount of the filler added. This trend was also true as regards the composite zone in castings, where a significant refinement and increased surface content of the TiC precipitates was observed.
    W pracy omówiono metodę wytwarzania stref kompozytowych w odlewach z ferrytyczno-perlitycznego żeliwa sferoidalnego. Faza wzmacniająca strefy kompozytowej był węglik tytanu (TiC), uzyskany w wyniku syntezy in situ substratów wprowadzonych do formy w postaci wyprasek. Do kompozycji substratów reakcji syntezy TiC wprowadzono wypełniacz, proszek Fe w ilości 10 i 50 %mas. w celu zbadania możliwości zmiany twardości strefy kompozytowej. Dodatek wypełniacza spowodował zmiane udziału powierzchniowego oraz średniej wielkości TiC. W przypadku 50 %mas. dodatku wypełniacza otrzymano dziesięciokrotne zmniejszenie wymiarów węglików. Analizowano zmiany mechaniczne w obrębie strefy, badając jej twardość HV. Badana wykazały stopniowy spadek twardości strefy wraz z ilością dodawanego wypełniacza. Tendencja ta dotyczyła również strefy kompozytowej odlewu, w którym stwierdzono znaczne rozdrobnienie wydzieleń TiC i wzrost ich udziału powierzchniowego.
    Źródło:
    Archives of Metallurgy and Materials; 2013, 58, 2; 465-471
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Locally Reinforcement TiC-Fe Type Produced in Situ in Castings
    Autorzy:
    Olejnik, E.
    Szymański, Ł.
    Kurtyka, P.
    Tokarski, T.
    Maziarz, W
    Grabowska, B.
    Czapla, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/380995.pdf
    Data publikacji:
    2016
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    MMCs
    reinforcement
    TiC
    in situ
    hardness
    ball-on-disc
    zbrojenie
    twardość
    Opis:
    Refinement is one of the most energy consuming technological process, aimed at obtaining mineral raw materials of the proper grain size. Cast structural elements such as jaws or hammers in crushing machines operate under conditions of an intensive wear. The data indicate that 80% of failures of machines and devices is caused by wearing of rubbing surfaces. This problem became the subject of several scientific and industrial investigations carried out in the whole world in order to produce materials ultra- wear resistant. Methods allowing to obtain wear resistant composite castings are discussed in the hereby paper. Within the performed research microstructures of the produced composite zones were presented and the comparative analysis with regard to mechanical and functional properties of local composite reinforcements in relation to the commercial alloys of increased wear resistance was performed. The results show almost twenty five times increase in wear resistance compared to manganese cast steel containing 18% Mn.
    Źródło:
    Archives of Foundry Engineering; 2016, 16, 3; 77-82
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Strefy kompozytowe otrzymywane in situ w staliwnych odlewach bijaków do kruszarek
    Composite zones obtained in situ in steel casts of crushing mill beaters
    Autorzy:
    Opitek, B.
    Olejnik, E.
    Lelito, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/391423.pdf
    Data publikacji:
    2018
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Odlewnictwa
    Tematy:
    MMCs
    TiC
    in situ
    lokalne wzmocnienie
    mikrostruktura
    kruszarka
    local reinforcement
    microstructure
    crushing mill
    Opis:
    Prezentowana praca miała na celu uzyskanie elementu bijaka do kruszarki wykorzystywanego w warunkach dużego zużycia ściernego oraz pracującego pod wysokimi naciskami. Wytworzono, metodą SHSB, lokalną strefę kompozytową składającą się z bardzo twardego węglika tytanu – TiC. Umieszczone w przygotowanej wcześniej formie odlewniczej wypraski zostały zalane ciekłym metalem, którego ciepło spowodowało zainicjowanie reakcji in situ tworzenia się węglika tytanu. Otrzymany w ten sposób odlew poddano badaniom. Wykonano analizę składu fazowego na dyfraktometrze rentgenowskim – XRD. Dodatkowo przeprowadzono badania na elektronowym mikroskopie skaningowym – SEM w celu określenia kształtu, wielkości i rozmieszczenia TiC. W efekcie przeprowadzonych prac i badań otrzymano materiał wysokiej jakości zgodny z oczekiwaniami.
    The aim of the presented study was to obtain the element of a crushing mill beater reinforced with a composite zone, working under the conditions of high abrasive wear as well as high pressures. By means of the SHSB method, a local composite zone was created consisting of very hard titanium carbide – TiC. The moulded pieces prepared beforehand in the casting mould were filled with liquid metal, whose heat caused the initiation of an in situ reaction – the formation of titanium carbide. The cast obtained in this way was subjected to tests. An analysis of the physical composition was performed on an X-ray diffractometer – XRD. Additionally, investigations with the use of a scanning electron microscope SEM were carried out in order to determine the shape, size and distribution of TiC. As a result of the conducted research, a high quality material was obtained, which was in line with the authors' expectations.
    Źródło:
    Prace Instytutu Odlewnictwa; 2018, 58, 3; 191-199
    1899-2439
    Pojawia się w:
    Prace Instytutu Odlewnictwa
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies