Welded joint cracking in martensitic stainless steel precipitation-sthregthened with copper
Pękanie złącz spawanych stali nierdzewnej martenzytycznej utwardzanej wydzieleniowo miedzią - Autorzy:
-
Ziewiec, A.
Czech, J.
Tasak, E. - Powiązania:
- https://bibliotekanauki.pl/articles/356169.pdf
- Data publikacji:
- 2012
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
17-4PH grade
Weldability Testing
copper
liquid metal embrittlement
stainless steel
GTAW
fracture - Opis:
-
Problem of welded joint cracking in the HAZ of Cu strengthened 17-4PH grade precipitation hardening martensitic stainless steel is presented. Hypothesis concerning hydrogen embrittlement origin of the cracks is opposed. It was concluded that the cracks located in the high-temperature zone of the HAZ exhibit characteristics of hot cracks which originated as a result of steel embrittlement in the presence of Cu rich liquid phase. The mechanism of steel surface enrichment in Cu is proposed. Practical methods of cracks elimination are presented.
W artykule przedstawiono problem pękania w strefie wpływu ciepła stali nierdzewnej martenzytycznej utwardzanej wydzieleniowo miedzią. Podważono literaturowe informacje wskazując, ze sa to pęknięcia zimne spowodowane kruchością wodorowa. Stwierdzono, ze pęknięcia zlokalizowane w wysokotemperaturowym obszarze SWC maja charakter pęknięć gorących i powstały w wyniku kruchości stali w obecności cieczy bogatej w miedz. Wyjaśniono mechanizm wzbogacania się powierzchni stali w miedz oraz podano technologiczny sposób eliminacji pęknięć. - Źródło:
-
Archives of Metallurgy and Materials; 2012, 57, 4; 1055-1061