Tytuł:: Examinations of Steel Overlap Joints Obtained Using the Friction Stir Welding Technology
Autorzy:: Więckowski, W.
Lacki, P.
Adamus, J.
Powiązania:: https://bibliotekanauki.pl/articles/356481.pdf
Data publikacji:: 2019
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: friction stir welding
FSW
1.4541 steel
Opis:: The aim of the study was to analyse mechanical properties and microstructure of joints obtained using friction stir welding (FSW) technology. The focus of the study was on overlap linear FSW joints made of 1.4541 DIN 17441 steel sheets with thickness of 1.2 mm. Tools used during friction stir welding of steel joints were made of W-Re alloy. The joints were subjected to visual inspection and their load bearing capacity was evaluated by means of the tensile strength test with analysis of joint breaking mechanism. Furthermore, the joints were also tested during metallographic examinations. The analysis performed in the study revealed that all the samples of the FSW joints were broken outside the joint area in the base material of the upper sheet metal, which confirms its high tensile strength. Mean load capacity of the joints was 15.8 kN. Macroscopic and microscopic examinations of the joints did not reveal significant defects on the joint surface and in the cross-sections.
Źródło:: Archives of Metallurgy and Materials; 2019, 64, 1; 393-399
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: The effect of tool wear on the quality of lap joints between 7075 t6 aluminum alloy sheet metal created with the FSW method
Wpływ zużycia narzędzia na jakość połączeń zakładkowych blach ze stopu Aluminium 7075 T6 wykonanych metodą FSW
Autorzy:: Burek, R.
Wydrzyński, D.
Sęp, J.
Więckowski, W.
Powiązania:: https://bibliotekanauki.pl/articles/1365376.pdf
Data publikacji:: 2018
Wydawca:: Polska Akademia Nauk. Polskie Naukowo-Techniczne Towarzystwo Eksploatacyjne PAN
Tematy:: friction stir welding
FSW
Al 7075 T6 alloy
zgrzewanie tarciowe z przemieszaniem
Al 7075 T6
Opis:: The article concerns the issues of tool wear effect on the quality of a friction stir welding joint quality. The experiment used aluminum alloy 7075 T6 sheet metal, which is used primarily in the aerospace industry. 1.0mm and 0.8mm thick lap joints were tested. Tool wear was determined based on multiple readings on a multisensory machine. The tool wear evaluation was done on the basis of a static tensile strength test and metallographic sections of the joints. The pin of the tool works in more demanding conditions and is more exposed to friction. This results from tooling operations performed at full depth dive in the jointed material. When also considering the small dimensions of the pin such as the diameter and the great forces occurring in this process, it is easy to see why this element is most susceptible to tool wear. The welding process causes the tool to undergo friction wear, which is the cause of reduced tool dive depth in the jointed material. As a result, it is paramount to constantly control the tool extension to achieve the desired quality parameters of the joint. After creating 200m of joints, a decrease in the strength of joints was observed as well as the repeatability of the results connected to a change in the stirring conditions in the material. The change in joint strength and tool wear is also confirmed in the metallographic analysis, which states that the continued degradation of the tool makes it subject to a decrease in size of the characteristic sizes of the thermoplastic zone that is the main determining factor of the joint strength.
Opracowanie podejmuje problematykę wpływu zużycia narzędzia na jakość zgrzeiny otrzymanej metodą zgrzewania tarciowego z przemieszaniem FSW. Do badań użyto stopu aluminium Al 7075 T6, stosowanego głównie w przemyśle lotniczym. Badano połączenia zakładkowe blach o grubości 1,0mm i 0,8mm. Zużycie narzędzia oceniano na podstawie pomiarów na maszynie multisensorycznej. Ocenę wpływu zużycia przeprowadzono w oparciu o statyczną próbę rozciągania oraz analizę zgładów metalograficznych wykonanych połączeń.Trzpień narzędzia pracuje w trudniejszych warunkach i jest bardziej narażony na ścieranie. Wynika to z pracy przy pełnym zagłębieniu w łączonym materiale. Zważywszy również na stosunkowo małe wymiary trzpienia tj. jego średnicę i duże siły występujące w procesie to ten element jest najbardziej narażony na zużycie. W procesie zgrzewania narzędzie ulega zużyciu ściernemu, co jest powodem zmniejszania zagłębienia narzędzia w materiale łączonym. W związku z powyższym konieczna jest ciągła kontrola wysunięcia narzędzia dla uzyskania pożądanych parametrów jakościowych zgrzeiny. Po wykonaniu 200m zgrzeiny zauważono zmniejszenie wytrzymałości zgrzeiny, jak również powtarzalności wyników związany ze zmianą warunków mieszania materiału. Zmiana wytrzymałości zgrzeiny oraz zużycia narzędzia ma również potwierdzenie w badaniach metalograficznych, z których wynika, iż w związku z postępującą degradacją narzędzia zmniejszeniu ulegają wymiary charakterystyczne strefy termo–plastycznej odpowiedzialnej w główniej mierze za wytrzymałość zgrzeiny.
Źródło:: Eksploatacja i Niezawodność; 2018, 20, 1; 100-106
1507-2711
Pojawia się w:: Eksploatacja i Niezawodność
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Więckowski, J." wg kryterium: Autor

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język