- Tytuł:
- A Comparative Study on the Corrosion Behaviour of Gas Nitrided and TiAlN Coated AISI D2 Steel by Thermo-Reactive Diffusion Technique
- Autorzy:
-
Cegil, O.
Sen, U.
Sen, S. - Powiązania:
- https://bibliotekanauki.pl/articles/1399731.pdf
- Data publikacji:
- 2013-02
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.05.Je
81.65.Kn - Opis:
- In this study, the corrosion behaviors of nitride and titanium aluminum nitride (TiAlN) layers deposited on AISI D2 steel samples are reported. Steel was at first nitrided in a nitrogen and ammonia atmosphere at 575C for 8 h and then titanium nitride coating treatment was performed in the powder mixture consisting of ferro-titanium, aluminum, ammonium chloride and alumina at 1000C for 2 h by thermo-reactive diffusion technique. Phase analysis and corrosion tests were realized on the titanium aluminum nitride coated steel. The corrosion properties of uncoated and coated samples were characterized by potentiostatic polarization test. The tests were conducted using a three-electrode system test unit with a platinum counter electrode of $2.269 cm^2$ and an Ag/AgCl, 3 M KCl electrode as the reference electrode. Nitrided and TiAlN coated steel specimens exhibited higher corrosion resistance than uncoated steel in 0.5 M $H_2SO_4$ solution. Conclusively, the application of nitride and TiAlN films on AISI D2 steel increased surface hardness and corrosion resistance. TiAlN coating exhibits the highest corrosion resistance.
- Źródło:
-
Acta Physica Polonica A; 2013, 123, 2; 265-267
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł