- Characterization of $Ni_3Al$ and $Ti_3Al$ Coatings Produced by Electric Current Activated Sintering Method
- Autorzy:
-
Ergin, N.
Yoruk, G.
Ozdemir, O. - Powiązania:
- https://bibliotekanauki.pl/articles/1399712.pdf
- Data publikacji:
- 2013-02
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.20.Ev
81.40.Pq - Opis:
- The present study reports on $Ni_3Al$ and $Ti_3Al$-based intermetallics coated on AISI 1010 steel substrate by one-step pressure assisted electric current activated sintering method. Ni, Ti, and Al elemental powders were mixed in the stoichiometric ratio corresponding to the $Ni_3Al$ and $Ti_3Al$ intermetallics at molar proportion of 3:1. The mixed coating powders were placed onto the steel substrate in a mold, and pressed with compressive stress of 100 MPa and then, electric current: 1100-1200 A, voltage 2.9-3.4 V was applied for 15 min during coating. As-synthesized coatings seem to have good adherence with many small porosities. The phases formed in the $Ni_3Al$ coating layer were $Ni_3Al$ as a major phase beside NiO and $NiAl_2O_4$ trace phases, which were confirmed by X-ray diffraction analysis. However, TiAl and Ti trace phases besides major $Ti_3Al$ phase were detected in the $Ti_3Al$ coating. The hardness of the $Ni_3Al$, $Ti_3Al$ coatings and AISI 1010 substrate was approximately 321 ± 18, 445 ± 13 and 157 $HV_{0.5}$, respectively.
- Źródło:
-
Acta Physica Polonica A; 2013, 123, 2; 245-247