- Tytuł:
- Characterization of TiAl-Be Alloys Produced by Electric Current Activated Sintering
- Autorzy:
-
Ergin, N.
Ozdemir, O. - Powiązania:
- https://bibliotekanauki.pl/articles/1401293.pdf
- Data publikacji:
- 2015-04
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.05.Bx
81.20.Ev
81.40.Cd - Opis:
- In this study, TiAl-Be intermetallic alloys were produced by electric current-activated sintering (ECAS) method in open air under the uniaxial pressure of 200 MPa at a current of 1100-1200 A, applied for 2 minutes. Aluminum powder with 15 μm size (99%), titanium powder with less than 45 μm size (99.5%) and beryllium powder with size less than 44 μm size (99%) were used in order to produce the samples. The elemental powders were mixed in the stoichiometric ratio of 1:1, corresponding to molar proportion of TiAl intermetallic phases, and then the mixed powders were synthesized. While three phases were found in the TiAl samples after the microstructural examination, multi-phases were observed in the TiAl-5 wt.% Be samples. XRD studies revealed that the TiAl intermetallic alloys include TiAl, Ti₃Al and TiAl₃ phases. In addition to these three phases, Be₂Ti phase was also found in the TiAl-5 wt.% Be alloys. The relative densities of the TiAl and TiAl-5 wt.% Be samples, measured according to Archimedes' principle, were approximately 96.4% and 94.5%. Micro-hardness of TiAl and TiAl-5 wt.% Be samples was approximately 426± 34 and 478± 62 $HV_{0.1}$, respectively.
- Źródło:
-
Acta Physica Polonica A; 2015, 127, 4; 1103-1105
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł