Implantation Temperature Effects on the Nanoscale Optical Pattern Fabrication in a-SiC:H Films by $Ga^{+}$ Focused Ion Beams
Autorzy:
Tsvetkova, T.
Wright, C.
Hosseini, P.
Bischoff, L.
Zuk, J.
Powiązania:
https://bibliotekanauki.pl/articles/1400488.pdf
Data publikacji:
2013-05
Wydawca:
Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:
85.40.Hp
81.16.Rf
68.55.Ln
Opis:
This work is related to a novel approach of providing some new generation ultrastable (> 50 years), ultrahigh density (> 1 Tbit/sq.in.) data storage for archival applications. We used ion-implantation to write nanoscale data into hydrogenated amorphous silicon carbide (a-SiC:H) films. Wide bandgap a-SiC:H samples, $Ga^{+}$ focused ion beam implanted, have been prepared. A range of samples has been focused ion beam patterned under different implantation conditions, with emphasis on different substrate temperatures (typically from 0C temperature to around room temperature). Some of the room temperature implanted samples were further annealed at + 250C in vacuum. The focused ion beam patterned samples were then analysed using near-field techniques, like atomic force microscopy, to define optimum implantation conditions and the resulting consequences for archival data storage applications. The atomic force microscopy analysis of $Ga^{+}$ focused ion beam implanted $a-Si_{1-x}C_{x}:H$ samples at room temperature and at 0C revealed an increase of both the depth and the width of the individual lines within the focused ion beam written patterns at the lower temperature, as a result of an increased ion beam induced sputtering yield, in good agreement with the previous results for the case of $Ga^+$ broad beam implantation in $a-Si_{1-x}C_{x}:H$ and again suggesting that the best conditions for optical data storage for archival storage applications would be using $Ga^+$ ion implantation in a-SiC:H films with an optimal dose at room temperatures. Similarly, the atomic force microscopy results confirm that no advantage is expected to result from post-implantation annealing treatments.
Źródło:
Acta Physica Polonica A; 2013, 123, 5; 952-955
0587-4246
1898-794X
Pojawia się w:
Acta Physica Polonica A
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies