- Tytuł:
- Influence of Al₂O₃ Particles Weight Fraction on Fracture Mechanism of AZ61 Mg-Al₂O₃ System Studied by In Situ Tensile Test in SEM
- Autorzy:
-
Besterci, M.
Nagy, Š.
Huang, S.
Velgosová, O.
Sülleiová, K.
Lin, P. - Powiązania:
- https://bibliotekanauki.pl/articles/1398687.pdf
- Data publikacji:
- 2016-01
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.05.-t
62.20.mm
62.23.Pq - Opis:
- In situ observation of AZ61 Mg alloy with 1 and 5 wt% of Al₂O₃ in the scanning electron microscopy was performed to study influence of the weight fraction of Al₂O₃ particles on the deformation and fracture mechanism during tensile test. Structure of the experimental materials was also analysed; microstructures were heterogeneous, with randomly distributed globular Al₂O₃ particles (average diameter of 25 nm) and Mg₁₇Al₁₂ intermetallic phase (average diameter of 0.4 μ m). It was shown that during tensile deformation the failure of Mg₁₇Al₁₂ particles and decohesion of the matrix-Al₂O₃ particles interphase boundary started simultaneously. Decohesion resulted from the different physical properties of matrix and Al₂O₃ particles. The influence of the Al₂O₃ weight fraction on the final fracture was evident; for material with 5 wt% of Al₂O₃, the fracture surface was approximately perpendicular to the loading direction and for material with 1 wt% of Al₂O₃ was at 45° angle. Fracture surface had transcrystalline ductile character.
- Źródło:
-
Acta Physica Polonica A; 2016, 129, 1; 138-141
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł