Tytuł:: Studies on the recrystalization of nanocrystalline metals
Autorzy:: Lendzion-Bieluń, Z.
Gleń, M.
Powiązania:: https://bibliotekanauki.pl/articles/778633.pdf
Data publikacji:: 2007
Wydawca:: Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie
Tematy:: kobalt nanokrystaliczny
rekrystalizacja
nanokrystaliczne metale
nanocrystalline cobalt
recrystalization
Opis:: The influence of the promoters such as CaO, Al2O3 and K2O on the specific surface area of the nanocrystalline cobalt was determined. The recrystalization process of the nanocrystalline cobalt was determined and compared with the examinations conducted on the iron catalyst for ammonia synthesis. The triply promoted nanocrystalline obtained cobalt after the annealing process, has got greater specific surface area than the triply promoted iron.
Źródło:: Polish Journal of Chemical Technology; 2007, 9, 4; 5-7
1509-8117
1899-4741
Pojawia się w:: Polish Journal of Chemical Technology
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Study of the anatase to rutile transformation kinetics of the modified TiO2
Autorzy:: Grzmil, B.
Gleń, M.
Kic, B.
Lubkowski, K.
Powiązania:: https://bibliotekanauki.pl/articles/779360.pdf
Data publikacji:: 2013
Wydawca:: Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie
Tematy:: TiO2
anatase
rutile
modification
phase transformation kinetics
Opis:: TiO2 attracts much interest because of its many potential applications. The use of titanium dioxide strongly depends on its polymorphic form: brookite, anatase, or rutile. Only rutile and anatase play an important role in industry. Anatase as a metastable form undergoes a non-reversible transformation into rutile. Understanding the kinetics of phase transformation and the processes of crystal growth of a material is essential for controlling its structure and, thus, its specific properties. The main purpose of this paper is to explain the anatase to rutile recrystallization kinetics in the modified TiO2 calcined from industrial hydrated titanium dioxide. The apparent activation energy of anatase to rutile transformation and the average size of titanium dioxide crystallites were determined for the unmodified TiO2 and TiO2 modified with P, K, Al, B, Zn, Zr, Ce, Sn, or Sb introduced in the amount of 0.5 mol% and 1.0 mol% when recalculated for their oxides. The growth of TiO2 crystallites during calcination was strongly inhibited by P, Ce and Zr, and inhibited to a lesser degree by Al, Sn and Sb. B and Zn did not affect the investigated process and K accelerated crystallites growth. The values of apparent activation energy depending on a modifier formed a relationship: Al
Źródło:: Polish Journal of Chemical Technology; 2013, 15, 2; 73-80
1509-8117
1899-4741
Pojawia się w:: Polish Journal of Chemical Technology
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Gleń, M." wg kryterium: Autor

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język