- Tytuł:
- Tribological wear of Fe-Al coatings applied by gas detonation spraying
- Autorzy:
- Chrostek, Tomasz
- Powiązania:
- https://bibliotekanauki.pl/articles/2069744.pdf
- Data publikacji:
- 2021
- Wydawca:
- Uniwersytet Warmińsko-Mazurski w Olsztynie
- Tematy:
-
gas detonation spraying
GDS
coating
Fe-Al
intermetallic alloys
tribology - Opis:
- Comparative tests of gas detonation (GDS) coatings were carried out in order to investigate the influence of spraying parameters on abrasive wear under dry friction conditions. The tests were carried out using the pin-on-disc (PoD) method at room temperature. The microstructure of the coatings was analysed by X-ray diffraction (XRD) and scanning electron microscopy (SEM/EDS) methods. The results showed that with certain parameters of the GDS process, the main phase of the produced coatings is the FeAl phase with the participation of thin oxide layers, mainly Al2O3. The tribological tests proved that the coatings sprayed with the shorter barrel of the GDS gun showed higher wear resistance. The coefficient of friction was slightly lower in the case of coatings sprayed with the longer barrel of the GDS gun. During dry friction, oxide layers form on the surface, which act as a solid lubricant. The load applied to the samples during the tests causes shear stresses, thus increasing the wear of the coatings. During friction, the surface of the coatings is subjected to alternating tensile and compressive stresses, which lead to delamination and is the main wear mechanism of the coatings.
- Źródło:
-
Technical Sciences / University of Warmia and Mazury in Olsztyn; 2021, 24(1); 245--256
1505-4675
2083-4527 - Pojawia się w:
- Technical Sciences / University of Warmia and Mazury in Olsztyn
- Dostawca treści:
- Biblioteka Nauki
Artykuł