Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "wroclaw, D." wg kryterium: Wszystkie pola

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-3 z 3
    Tytuł:
    Budowa budynków Wydziału Elektrycznego D1 i Wydziału Lotniczego D2 Politechniki Wrocławskiej – historia pewnej iluzji
    Construction of the Wrocław University of Technology buildings for the Faculty of Electrical Engineering D1 and Faculty of Aviation Engineering D2 – history of some illusion
    Autorzy:
    Bocheński, S.
    Piskozub, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/217279.pdf
    Data publikacji:
    2015
    Wydawca:
    Stowarzyszenie Konserwatorów Zabytków
    Tematy:
    rewaloryzacja zabytków
    architektura socrealistyczna
    Politechnika Wrocławska
    monument restoration
    socialist realist architecture
    Wrocław University of Technology
    Opis:
    Spostrzeżenia poczynione w trakcie rozpoczętego w 2013 roku remontu elewacji budynku Wydziału Elektrycznego D1 Politechniki Wrocławskiej skłoniły autorów prezentowanego artykułu do przyjrzenia się historii powojennej rozbudowy kampusu Uczelni. Ambitna wizja olbrzymiego kompleksu obiektów ewoluowała w kolejnych koncepcjach, aby ostatecznie ograniczyć się do realizacji jedynie części dwóch budynków: D1 i D2. Ich bryły nie zostały zrealizowane w całości, w trakcie budowy wprowadzano oszczędności materiałowe, a niektóre elewacje do teraz nie zostały dokończone. Dziś jednak wartość tych obiektów należy docenić zarówno pod względem kompozycji architektonicznej, jak i jako świadectwo historii upadku idei socrealizmu.
    The observations made during the facade restoration of the D1 building of the Wrocław University of Technology, Faculty of Electrical Engineering, have induced the authors of the presented article to examine the post-war history of the University campus extension. The ambitious vision of huge complex of objects evolved in successive concepts, and fi nally has been limited to the realization of only parts of two buildings: D1 and D2. Their solid bodies have not been fully completed, during their construction several material savings were introduced, and some facades have remained unfi nished until now. Today, however, the value of these objects should be appreciated, both concerning their architectural composition and as the historical testimony of the collapse of socialistic ideas.
    Źródło:
    Wiadomości Konserwatorskie; 2015, 41; 65-73
    0860-2395
    2544-8870
    Pojawia się w:
    Wiadomości Konserwatorskie
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Beton Hali Stulecia (UNESCO List) we Wrocławiu
    Concrete of the Centennial Hall (UNESCO List), Wrocław, Poland
    Autorzy:
    Jasieńko, J.
    Moczko, M.
    Wala, D.
    Powiązania:
    https://bibliotekanauki.pl/articles/218232.pdf
    Data publikacji:
    2011
    Wydawca:
    Stowarzyszenie Konserwatorów Zabytków
    Tematy:
    Hala Stulecia we Wrocławiu
    beton
    Centennial Hall
    concrete
    Opis:
    W pracy przedstawiono wyniki badań cech mechanicznych i fizycznych betonu w dolnym pierścieniu obwodowym kopuły Hali Stulecia we Wrocławiu, które zostały przeprowadzone w drugiej połowie 2009 roku, w czasie robót remontowych elewacji tego obiektu. Przedstawione wyniki dokumentują aktualne cechy mechaniczno-fizyczne betonu, po upływie około 100 lat. Z jednej strony są one unikalnym źródłem informacji o jakości betonu z początku XX wieku, z drugiej zaś pozwalają na ocenę uwarunkowań trwałości tego tworzywa po upływie stulecia. Uzyskane wyniki wykazały, że aktualny stan techniczny betonu, pomimo upływu niemal 100 lat, należy uznać za bardzo dobry. Parametry wytrzymałościowe tego betonu odpowiadają obecnym wymaganiom stawianym klasie wytrzymałości C20/25, co biorąc pod uwagę poziom technologii betonu na początku ubiegłego wieku, należy uznać za wynik nadspodziewanie dobry. Wysoką jakość badanego betonu potwierdzają także wyniki badania wytrzymałości betonu na rozciąganie, które wykazały jej średnią wartość na poziomie około 3,6 MPa oraz wyniki oznaczenia nasiąkliwości, której wartości zawierały się w przedziale od 3,9% do 4,8%, przy współczynniku zmienności równym 8%, co świadczy o dużej szczelności i jednorodności strukturalnej badanego betonu. Badania wykazały także, że przypowierzchniowa warstwa badanego betonu uległa w znacznym stopniu procesowi karbonatyzacji. W większości badanych przypadków stwierdzono, że zasięg karbonatyzacji jest nie mniejszy niż 35 mm, przy czym wyniki badań, które zostały wykonane w kierunku prostopadłym do kierunku betonowania, pokazały, że w wielu miejscach beton pomimo upływu niemal 100 lat nie uległ temu procesowi i w pełni zachował zdolności pasywacyjne w stosunku do stali zbrojeniowej.
    The work presents results of tests of mechanical and physical properties of concrete in the bottom perimeter ring of the dome of the Centennial Hall in Wrocław, conducted in the second half of 2009 during renovation work on the object elevation. The presented results document current mechanical and physical properties of concrete, after almost one hundred years have passed. On the one hand, they are a unique source of information about the quality of concrete from the beginning of the 20th century, while on the other, they allow for evaluation of durability conditions of the material after a century. The obtained results showed that the current technical condition of concrete, although almost 100 years have passed, should be regarded as very good. Strength parameters of that concrete meet the current requirements for strength class C20/25 which, considering the level of concrete technology at the beginning of the previous century should be considered a surprisingly good result. High quality of the tested concrete was confirmed by the results of the concrete tensile strength tests, which indicated its average value at the level of approximately 3.6 MPa, and the results of absorbability determination the values of which were between 3.9% and 4.8%, with the coefficient of variation equalling 8%, which proves significant density and structural homogeneity of the examined concrete. The tests also showed that the surface layer of the examined concrete underwent the process of carbonatisation to a great extent. In the majority of examined cases it was found out that the range of carbonatisation is not smaller than 35 mm and, moreover, results of tests which were carried out in the direction perpendicular to the direction of concreting showed that in many places concrete did not undergo the process and fully maintained its passivation properties in relation to reinforcing steel, despite the passing of almost 100 years.
    Źródło:
    Wiadomości Konserwatorskie; 2011, 30; 168-176
    0860-2395
    2544-8870
    Pojawia się w:
    Wiadomości Konserwatorskie
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Wybrane badania betonu Hali Stulecia we Wrocławiu (obiekt UNESCO)
    Selected research on concrete of the Centennial Hall in Wroclaw (UNESCO site)
    Autorzy:
    Jasieńko, J.
    Bednarz, Ł.
    Piechówka-Mielnik, M.
    Łydżba, D.
    Rajczakowska, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/217171.pdf
    Data publikacji:
    2015
    Wydawca:
    Stowarzyszenie Konserwatorów Zabytków
    Tematy:
    Hala Stulecia
    beton
    właściwości fizyczne
    właściwości chemiczne
    mikrostruktura
    porowatość
    indentacja
    Centennial Hall
    concrete
    physical
    properties
    chemical properties
    microstructure
    porosity
    indentation technique
    Opis:
    W pracy przedstawiono wyniki badań właściwości chemicznych i fizycznych betonu znajdującego się w dolnym pierścieniu obwodowym kopuły Hali Stulecia w Wrocławiu. Badania przeprowadzone były w drugiej połowie 2009 roku oraz w pierwszej połowie 2015 roku. Ponadto wykonano dodatkowo badania mikrostruktury betonu przy użyciu tomografu komputerowego oraz, na podstawie serii testów nanoindentacji, wykonanych w nanoindenterze. Dotychczas przeprowadzone badania potwierdzają wysoką jakość betonu. Kruszywo znajdujące się w badanych próbkach to w większości łamany granit strzegomski. W kruszywie o frakcjach poniżej 8 mm zaobserwowano występowanie żużlu paleniskowego o dużej porowatości oraz wtrącenia w postaci ścinków drewnianych. Ocenę składu mineralogicznego betonu wykonano wykorzystując wyniki analizy składu tlenkowego. Przez zmniejszoną zawartość CaO skład tlenkowy zbliżony jest do składu cementu hutniczego. Wprowadzając świadomie do mieszanki betonowej żużel paleniskowy uzyskano zwartą mikrostrukturę betonu. Stwardniały zaczyn w badanym betonie wykazuje doskonałą przyczepność do łamanego kruszywa granitowego. Posiada strukturę zwartą, gęstą, o bardzo niskiej nasiąkliwości. Mikrotwardość badanego betonu wyniosła 1,8 GPa, a moduł sprężystości E = 33 GPa. W badaniach wykonanych za pomocą mikrotomografu komputerowego oznaczona porowatość w badanych próbkach wyniosła ok. 10%. W strukturze przeważają mikropory poniżej 300 μm.
    The paper reports on results of chemical and physical testing of concrete sampled from the lower circumferential ring of the dome of the Centennial Hall In Wrocław. Testing was conducted in the second half of 2009 and in the first half of 2015. Additionally, an analysis of the concrete microstructure was undertaken using a computer tomography and a number of nano-indentation tests were carried out with a nanoindentation device. Analysis of the concrete carried out to date confi rms high concrete quality. The aggregate in tested specimens comprises mainly crushed Strzegom granite. In aggregate fractions lower than 8 mm, the presence of high porosity slag and wood chip inclusions was observed. Analysis of concrete mineral composition was conducted using results of an oxide composition analysis. The oxide composition of this cement is close to the composition of blast-furnace cement. Introduction of slag into the concrete mix resulted in a dense microstructure of the concrete. The hardened cement paste in the tested concrete demonstrates excellent adhesion to crushed granite aggregate. This is characterised by a dense structure, with low absorbability. Micro-hardness of tested concrete was determined to equal 1,8 GPa and the modulus of elasticity E = 33 GPa. In studies conducted using micro-CT the porosity for tested samples found to be approximately 10%. In the structure the majority are micropores smaller than 300 μm.
    Źródło:
    Wiadomości Konserwatorskie; 2015, 42; 18-32
    0860-2395
    2544-8870
    Pojawia się w:
    Wiadomości Konserwatorskie
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies